Synthesis of cotton-like FeCoNi-Nd(OH)3 nanoparticles via reactive mechanical milling: Investigating chemical properties for cellular signaling applications

In this study, FeCoNi alloy nanoparticles were combined with Nd(OH)₃ nanostructures to create unique cotton-like nanoparticles (C-NPs). These C-NPs were synthesized through an accessible, two-step reactive chemical milling process. The nanoparticles originated from a blend of metal chlorides (FeCl₂, CoCl₂, and NiCl₂) and sodium (Na), used as a precursor in the reaction, within a SPEX milling apparatus. The Fe, Co, and Ni were maintained at equal weight percentages (1:1:1). Subsequently, NdCl₃ and Na were utilized to facilitate the attachment of Nd(OH)₃ nanostructures onto the FeCoNi nanoparticles through a solid-state reaction in the same SPEX milling setup. The Nd content was varied to investigate its effect on the integration of Nd(OH)₃ onto the surface of CoNiFe nanoparticles. Electron microscopy revealed the formation of cotton-like nanoparticles, and the distribution of elements was identified using secondary ion mass spectrometry. The CoNiFe alloy and Nd(OH)₃ phases were verified by X-ray diffraction analysis. These nanoparticles were internalized into cells via endocytosis, as observed in transmission electron microscopy images after incubation with the BT20 cell line (triple-negative breast cancer), likely due to interactions between –OH groups and the cell membrane. Following this, the cells containing C-NPs underwent photoluminescence studies, revealing two distinct emission peaks at 400 nm, and 486 nm. X-ray photoelectron spectroscopy indicated the presence of various heterostructures within the FeCoNi-Nd(OH)₃ complex, which may be responsible for these emission properties.