{"title":"胶体铂纳米粒子可增强树脂-牙本质粘接的耐久性。","authors":"Yuan Yuan , Papichaya Intajak , Norihito Sakaguchi , Shihchun Ting , Hongbo Zhang , Takatsumi Ikeda , Shuhei Hoshika , Hidehiko Sano , Atsushi Tomokiyo","doi":"10.1016/j.dental.2024.09.015","DOIUrl":null,"url":null,"abstract":"<div><h3>Objectives</h3><div>This study aims to investigate the effect of colloidal platinum nanoparticles (CPN) on the durability of resin-dentin bonding performance with contemporary adhesives.</div></div><div><h3>Methods</h3><div>Sixty non-carious human maxillary premolars were subjected to microtensile bond strength (µTBS) testing and divided into two main groups: CPN-treated and untreated. Within each group, specimens were randomly allocated to Clearfil Megabond 2 (MB2), Scotchbond Universal Plus Adhesive with self-etch mode (SE-SUP), and etch-and-rinse mode (ER-SUP) subgroups (n = 10/group). CPN was applied to dentin in the MB2 and SE-SUP groups for 20 s, followed by rinsing before adhesive application. In the ER-SUP group, CPN was applied after etch-and-rinse. The µTBS was tested after 24 h, 6 months, and 1 year, and the fracture modes were observed using SEM. The µTBS data were analyzed using a two-way ANOVA and post-hoc Tukey HSD test (α = 0.05). An additional twelve premolars underwent TEM/STEM/EDX for ultra-morphological observations.</div></div><div><h3>Results</h3><div>The application of CPN significantly prevented a decline in the µTBS of both the MB2 and SE-SUP groups. No significant decrease was observed in the ER-SUP group, either with aging or CPN application. Ultra-morphological images revealed platinum nanoparticles attaching to the collagen fibrils of the hybrid layer regardless of aging. It was highlighted that the nanoparticles attached to the banded collagen in the aging groups were observed.</div></div><div><h3>Significance</h3><div>CPN exhibits the potential in enhancing the longevity of resin-dentin bonding in SE mode.</div></div>","PeriodicalId":298,"journal":{"name":"Dental Materials","volume":"40 11","pages":"Pages 2034-2042"},"PeriodicalIF":4.6000,"publicationDate":"2024-11-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Colloidal platinum nanoparticles enhance resin-dentin bonding durability\",\"authors\":\"Yuan Yuan , Papichaya Intajak , Norihito Sakaguchi , Shihchun Ting , Hongbo Zhang , Takatsumi Ikeda , Shuhei Hoshika , Hidehiko Sano , Atsushi Tomokiyo\",\"doi\":\"10.1016/j.dental.2024.09.015\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><h3>Objectives</h3><div>This study aims to investigate the effect of colloidal platinum nanoparticles (CPN) on the durability of resin-dentin bonding performance with contemporary adhesives.</div></div><div><h3>Methods</h3><div>Sixty non-carious human maxillary premolars were subjected to microtensile bond strength (µTBS) testing and divided into two main groups: CPN-treated and untreated. Within each group, specimens were randomly allocated to Clearfil Megabond 2 (MB2), Scotchbond Universal Plus Adhesive with self-etch mode (SE-SUP), and etch-and-rinse mode (ER-SUP) subgroups (n = 10/group). CPN was applied to dentin in the MB2 and SE-SUP groups for 20 s, followed by rinsing before adhesive application. In the ER-SUP group, CPN was applied after etch-and-rinse. The µTBS was tested after 24 h, 6 months, and 1 year, and the fracture modes were observed using SEM. The µTBS data were analyzed using a two-way ANOVA and post-hoc Tukey HSD test (α = 0.05). An additional twelve premolars underwent TEM/STEM/EDX for ultra-morphological observations.</div></div><div><h3>Results</h3><div>The application of CPN significantly prevented a decline in the µTBS of both the MB2 and SE-SUP groups. No significant decrease was observed in the ER-SUP group, either with aging or CPN application. Ultra-morphological images revealed platinum nanoparticles attaching to the collagen fibrils of the hybrid layer regardless of aging. It was highlighted that the nanoparticles attached to the banded collagen in the aging groups were observed.</div></div><div><h3>Significance</h3><div>CPN exhibits the potential in enhancing the longevity of resin-dentin bonding in SE mode.</div></div>\",\"PeriodicalId\":298,\"journal\":{\"name\":\"Dental Materials\",\"volume\":\"40 11\",\"pages\":\"Pages 2034-2042\"},\"PeriodicalIF\":4.6000,\"publicationDate\":\"2024-11-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Dental Materials\",\"FirstCategoryId\":\"5\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S0109564124002860\",\"RegionNum\":1,\"RegionCategory\":\"医学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"DENTISTRY, ORAL SURGERY & MEDICINE\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Dental Materials","FirstCategoryId":"5","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0109564124002860","RegionNum":1,"RegionCategory":"医学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"DENTISTRY, ORAL SURGERY & MEDICINE","Score":null,"Total":0}
This study aims to investigate the effect of colloidal platinum nanoparticles (CPN) on the durability of resin-dentin bonding performance with contemporary adhesives.
Methods
Sixty non-carious human maxillary premolars were subjected to microtensile bond strength (µTBS) testing and divided into two main groups: CPN-treated and untreated. Within each group, specimens were randomly allocated to Clearfil Megabond 2 (MB2), Scotchbond Universal Plus Adhesive with self-etch mode (SE-SUP), and etch-and-rinse mode (ER-SUP) subgroups (n = 10/group). CPN was applied to dentin in the MB2 and SE-SUP groups for 20 s, followed by rinsing before adhesive application. In the ER-SUP group, CPN was applied after etch-and-rinse. The µTBS was tested after 24 h, 6 months, and 1 year, and the fracture modes were observed using SEM. The µTBS data were analyzed using a two-way ANOVA and post-hoc Tukey HSD test (α = 0.05). An additional twelve premolars underwent TEM/STEM/EDX for ultra-morphological observations.
Results
The application of CPN significantly prevented a decline in the µTBS of both the MB2 and SE-SUP groups. No significant decrease was observed in the ER-SUP group, either with aging or CPN application. Ultra-morphological images revealed platinum nanoparticles attaching to the collagen fibrils of the hybrid layer regardless of aging. It was highlighted that the nanoparticles attached to the banded collagen in the aging groups were observed.
Significance
CPN exhibits the potential in enhancing the longevity of resin-dentin bonding in SE mode.
期刊介绍：
Dental Materials publishes original research, review articles, and short communications.
Academy of Dental Materials members click here to register for free access to Dental Materials online.
The principal aim of Dental Materials is to promote rapid communication of scientific information between academia, industry, and the dental practitioner. Original Manuscripts on clinical and laboratory research of basic and applied character which focus on the properties or performance of dental materials or the reaction of host tissues to materials are given priority publication. Other acceptable topics include application technology in clinical dentistry and dental laboratory technology.
Comprehensive reviews and editorial commentaries on pertinent subjects will be considered.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们