重金属污染沉积物的水泥和沸石稳定/固化:841 天沥滤特性、机制和微观结构。

IF 7.1 2区 环境科学与生态学 Q1 ENGINEERING, ENVIRONMENTAL Waste management Pub Date : 2024-10-07 DOI:10.1016/j.wasman.2024.09.025
Nan Hu , Geng Chen , Yonghui Chen , Minguo Lin , Panpan Tang , Wanlu Zhang , Zi Ye
{"title":"重金属污染沉积物的水泥和沸石稳定/固化:841 天沥滤特性、机制和微观结构。","authors":"Nan Hu ,&nbsp;Geng Chen ,&nbsp;Yonghui Chen ,&nbsp;Minguo Lin ,&nbsp;Panpan Tang ,&nbsp;Wanlu Zhang ,&nbsp;Zi Ye","doi":"10.1016/j.wasman.2024.09.025","DOIUrl":null,"url":null,"abstract":"<div><div>The long-term effectiveness of stabilized/solidified sediments (S/S sediments) is increasingly attracting attention. This study investigated the long-term leaching characteristics and mechanisms of S/S sediment through an 841-day tank leaching test, considering the influence of cement content, curing time, and zeolite. The results indicate significant correlations among pH, heavy metals, TN, NH<sub>3</sub>-N, and COD. The specimens with 6 % cement cured for 30 days (C6(30)) demonstrated considerable heavy metal stabilization, with stabilization rates for Cr, Ni, Cu, Zn, As, and Pb reaching 99.81 %, 99.06 %, 98.93 %, 99.61 %, 97.58 %, and 99.97 %, respectively. Compared to C6(30), partial replacement of cement with 10 % zeolite (C5 + Z0.5(30)) not only more effectively stabilized heavy metals except As, but also reduced the release of COD and NH<sub>3</sub>-N by 4.23 % and 10.04 %, respectively. However, there was a risk of TN, NH<sub>3</sub>-N, and COD exceeding permissible limits during long-term leaching. Microscopic analysis results suggested that hydration products and low porosity contributed to stabilization of heavy metals. Leaching mechanisms was revealed that surface wash-off controls the leaching of Cr and Pb, while diffusion controls the leaching of Ni, Cu, Zn, As, COD, TN, and NH<sub>3</sub>-N. Considering stabilization performance, cost and carbon emissions, C5 + Z0.5(30) is an effective strategy for reducing long-term environmental risks of S/S sediments.</div></div>","PeriodicalId":23969,"journal":{"name":"Waste management","volume":"190 ","pages":"Pages 306-317"},"PeriodicalIF":7.1000,"publicationDate":"2024-10-07","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Cement and zeolite stabilization/solidification of heavy metal-contaminated sediments: 841-Day leaching characteristics, mechanisms, and microstructure\",\"authors\":\"Nan Hu ,&nbsp;Geng Chen ,&nbsp;Yonghui Chen ,&nbsp;Minguo Lin ,&nbsp;Panpan Tang ,&nbsp;Wanlu Zhang ,&nbsp;Zi Ye\",\"doi\":\"10.1016/j.wasman.2024.09.025\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><div>The long-term effectiveness of stabilized/solidified sediments (S/S sediments) is increasingly attracting attention. This study investigated the long-term leaching characteristics and mechanisms of S/S sediment through an 841-day tank leaching test, considering the influence of cement content, curing time, and zeolite. The results indicate significant correlations among pH, heavy metals, TN, NH<sub>3</sub>-N, and COD. The specimens with 6 % cement cured for 30 days (C6(30)) demonstrated considerable heavy metal stabilization, with stabilization rates for Cr, Ni, Cu, Zn, As, and Pb reaching 99.81 %, 99.06 %, 98.93 %, 99.61 %, 97.58 %, and 99.97 %, respectively. Compared to C6(30), partial replacement of cement with 10 % zeolite (C5 + Z0.5(30)) not only more effectively stabilized heavy metals except As, but also reduced the release of COD and NH<sub>3</sub>-N by 4.23 % and 10.04 %, respectively. However, there was a risk of TN, NH<sub>3</sub>-N, and COD exceeding permissible limits during long-term leaching. Microscopic analysis results suggested that hydration products and low porosity contributed to stabilization of heavy metals. Leaching mechanisms was revealed that surface wash-off controls the leaching of Cr and Pb, while diffusion controls the leaching of Ni, Cu, Zn, As, COD, TN, and NH<sub>3</sub>-N. Considering stabilization performance, cost and carbon emissions, C5 + Z0.5(30) is an effective strategy for reducing long-term environmental risks of S/S sediments.</div></div>\",\"PeriodicalId\":23969,\"journal\":{\"name\":\"Waste management\",\"volume\":\"190 \",\"pages\":\"Pages 306-317\"},\"PeriodicalIF\":7.1000,\"publicationDate\":\"2024-10-07\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Waste management\",\"FirstCategoryId\":\"93\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S0956053X24005130\",\"RegionNum\":2,\"RegionCategory\":\"环境科学与生态学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"ENGINEERING, ENVIRONMENTAL\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Waste management","FirstCategoryId":"93","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0956053X24005130","RegionNum":2,"RegionCategory":"环境科学与生态学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"ENGINEERING, ENVIRONMENTAL","Score":null,"Total":0}
引用次数: 0

摘要

稳定/固化沉积物(S/S 沉积物)的长期有效性越来越受到关注。考虑到水泥含量、固化时间和沸石的影响,本研究通过为期 841 天的槽浸出试验研究了 S/S 沉积物的长期浸出特性和机制。结果表明,pH 值、重金属、TN、NH3-N 和 COD 之间存在明显的相关性。水泥含量为 6%、固化时间为 30 天的试样(C6(30))表现出相当高的重金属稳定率,其中 Cr、Ni、Cu、Zn、As 和 Pb 的稳定率分别达到 99.81%、99.06%、98.93%、99.61%、97.58% 和 99.97%。与 C6(30) 相比,用 10% 的沸石部分替代水泥(C5 + Z0.5(30))不仅能更有效地稳定除 As 以外的重金属,还能将 COD 和 NH3-N 的释放量分别减少 4.23% 和 10.04%。不过,在长期浸滤过程中,TN、NH3-N 和 COD 仍有可能超过允许限值。显微分析结果表明,水化产物和低孔隙率有助于重金属的稳定。浸出机制显示,表面冲刷控制着铬和铅的浸出,而扩散控制着镍、铜、锌、砷、COD、TN 和 NH3-N 的浸出。考虑到稳定化性能、成本和碳排放,C5 + Z0.5(30)是降低 S/S 沉积物长期环境风险的有效策略。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Cement and zeolite stabilization/solidification of heavy metal-contaminated sediments: 841-Day leaching characteristics, mechanisms, and microstructure
The long-term effectiveness of stabilized/solidified sediments (S/S sediments) is increasingly attracting attention. This study investigated the long-term leaching characteristics and mechanisms of S/S sediment through an 841-day tank leaching test, considering the influence of cement content, curing time, and zeolite. The results indicate significant correlations among pH, heavy metals, TN, NH3-N, and COD. The specimens with 6 % cement cured for 30 days (C6(30)) demonstrated considerable heavy metal stabilization, with stabilization rates for Cr, Ni, Cu, Zn, As, and Pb reaching 99.81 %, 99.06 %, 98.93 %, 99.61 %, 97.58 %, and 99.97 %, respectively. Compared to C6(30), partial replacement of cement with 10 % zeolite (C5 + Z0.5(30)) not only more effectively stabilized heavy metals except As, but also reduced the release of COD and NH3-N by 4.23 % and 10.04 %, respectively. However, there was a risk of TN, NH3-N, and COD exceeding permissible limits during long-term leaching. Microscopic analysis results suggested that hydration products and low porosity contributed to stabilization of heavy metals. Leaching mechanisms was revealed that surface wash-off controls the leaching of Cr and Pb, while diffusion controls the leaching of Ni, Cu, Zn, As, COD, TN, and NH3-N. Considering stabilization performance, cost and carbon emissions, C5 + Z0.5(30) is an effective strategy for reducing long-term environmental risks of S/S sediments.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
Waste management
Waste management 环境科学-工程:环境
CiteScore
15.60
自引率
6.20%
发文量
492
审稿时长
39 days
期刊介绍: Waste Management is devoted to the presentation and discussion of information on solid wastes,it covers the entire lifecycle of solid. wastes. Scope: Addresses solid wastes in both industrialized and economically developing countries Covers various types of solid wastes, including: Municipal (e.g., residential, institutional, commercial, light industrial) Agricultural Special (e.g., C and D, healthcare, household hazardous wastes, sewage sludge)
期刊最新文献
Assessing the resource potential of paper and board in lightweight packaging waste sorting plants through manual analysis and sensor-based material flow monitoring. Losses and emissions in polypropylene recycling from household packaging waste. Selective collection of absorbent hygienic products: The results of a pilot test and waste characterization. Numerical study of rainfall percolation through a novel capillary barrier cover with a zipper-shape interface between fine- and coarse-grained soils. Conversion of the solid fraction of food waste separated by a screw press using an integrated hydrothermal carbonization and anaerobic digestion process
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1