利用四面体热电材料 Cu12Sb4S13 中 Cu 和 S 位点的双重置换来提高功率因数

IF 3.4 3区 化学 Q2 CHEMISTRY, INORGANIC & NUCLEAR Solid State Sciences Pub Date : 2024-10-23 DOI:10.1016/j.solidstatesciences.2024.107729
{"title":"利用四面体热电材料 Cu12Sb4S13 中 Cu 和 S 位点的双重置换来提高功率因数","authors":"","doi":"10.1016/j.solidstatesciences.2024.107729","DOIUrl":null,"url":null,"abstract":"<div><div>Thermoelectric (TE) materials-based devices are valuable for translating heat into electricity, but the cost is largely driven by the use of purified metals required for efficient TE performance. This study focuses on tetrahedrite materials, which are cost-effective due to their abundance in copper ore mining waste and status as one of the most widespread sulfosalts on Earth. The research investigates the effects of co-doping and iso-valent doping on the TE properties of p-type tetrahedrite samples, specifically Cu<sub>10</sub>Mn<sub>2</sub>Sb<sub>4</sub>S<sub>11</sub>Se<sub>2</sub> (Sample A) and Cu<sub>10</sub>MnZnSb₄S<sub>11</sub>Se<sub>2</sub> (Sample B). These samples were synthesized using hot pressing at 773 K and compared with the existing pristine compound (Cu<sub>10</sub>Mn<sub>2</sub>Sb<sub>4</sub>S<sub>13</sub>). Doping with Mn and Zn (1:1) at the Cu site was found to optimize carrier concentration and enhance phonon scattering, leading to an improved power factor. Additionally, the Se substitution at the S site also introduced band degeneracy, further increasing the power factor. Further, sample B exhibited the highest Seebeck coefficient (∼300 μV/K) at 650 K, in comparison to Sample A (∼225 μV/K) and the pristine compound (∼250 μV/K). On the other hand, Sample A demonstrated significantly higher electrical conductivity (∼0.76 × 10⁴ S/m at 650 K), ∿ three times greater than that of the other prepared samples. Notably, the power factor of Sample A (∼0.389 mW/mK<sup>2</sup> at 650 K) was more than twice that of Sample B (∼0.141 mW/mK<sup>2</sup>) and the pristine compound (∼0.160 mW/mK<sup>2</sup>). These findings suggest that dual-site substitution at the Cu and S positions presents a promising strategy to augment the TE performance of tetrahedrite compounds.</div></div>","PeriodicalId":432,"journal":{"name":"Solid State Sciences","volume":null,"pages":null},"PeriodicalIF":3.4000,"publicationDate":"2024-10-23","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Achieving enhanced power factor using dual substitution at Cu and S sites in tetrahedrites thermoelectric materials Cu12Sb4S13\",\"authors\":\"\",\"doi\":\"10.1016/j.solidstatesciences.2024.107729\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><div>Thermoelectric (TE) materials-based devices are valuable for translating heat into electricity, but the cost is largely driven by the use of purified metals required for efficient TE performance. This study focuses on tetrahedrite materials, which are cost-effective due to their abundance in copper ore mining waste and status as one of the most widespread sulfosalts on Earth. The research investigates the effects of co-doping and iso-valent doping on the TE properties of p-type tetrahedrite samples, specifically Cu<sub>10</sub>Mn<sub>2</sub>Sb<sub>4</sub>S<sub>11</sub>Se<sub>2</sub> (Sample A) and Cu<sub>10</sub>MnZnSb₄S<sub>11</sub>Se<sub>2</sub> (Sample B). These samples were synthesized using hot pressing at 773 K and compared with the existing pristine compound (Cu<sub>10</sub>Mn<sub>2</sub>Sb<sub>4</sub>S<sub>13</sub>). Doping with Mn and Zn (1:1) at the Cu site was found to optimize carrier concentration and enhance phonon scattering, leading to an improved power factor. Additionally, the Se substitution at the S site also introduced band degeneracy, further increasing the power factor. Further, sample B exhibited the highest Seebeck coefficient (∼300 μV/K) at 650 K, in comparison to Sample A (∼225 μV/K) and the pristine compound (∼250 μV/K). On the other hand, Sample A demonstrated significantly higher electrical conductivity (∼0.76 × 10⁴ S/m at 650 K), ∿ three times greater than that of the other prepared samples. Notably, the power factor of Sample A (∼0.389 mW/mK<sup>2</sup> at 650 K) was more than twice that of Sample B (∼0.141 mW/mK<sup>2</sup>) and the pristine compound (∼0.160 mW/mK<sup>2</sup>). These findings suggest that dual-site substitution at the Cu and S positions presents a promising strategy to augment the TE performance of tetrahedrite compounds.</div></div>\",\"PeriodicalId\":432,\"journal\":{\"name\":\"Solid State Sciences\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":3.4000,\"publicationDate\":\"2024-10-23\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Solid State Sciences\",\"FirstCategoryId\":\"92\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S1293255824002942\",\"RegionNum\":3,\"RegionCategory\":\"化学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"CHEMISTRY, INORGANIC & NUCLEAR\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Solid State Sciences","FirstCategoryId":"92","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S1293255824002942","RegionNum":3,"RegionCategory":"化学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"CHEMISTRY, INORGANIC & NUCLEAR","Score":null,"Total":0}
引用次数: 0

摘要

基于热电(TE)材料的设备在将热能转化为电能方面具有重要价值,但其成本在很大程度上取决于使用高效热电性能所需的纯化金属。本研究的重点是四面体材料,由于其大量存在于铜矿废料中,并且是地球上最常见的硫化物之一,因此成本效益很高。研究调查了共掺杂和同价掺杂对 p 型四面体样品 TE 性能的影响,特别是 Cu10Mn2Sb4S11Se2(样品 A)和 Cu10MnZnSb₄S11Se2(样品 B)。这些样品是在 773 K 下通过热压合成的,并与现有的原始化合物(Cu10Mn2Sb4S13)进行了比较。研究发现,在 Cu 位点掺入 Mn 和 Zn(1:1)可优化载流子浓度并增强声子散射,从而提高功率因数。此外,在 S 位点硒的替代也引入了带变性,进一步提高了功率因数。此外,与样品 A(∼225 μV/K)和原始化合物(∼250 μV/K)相比,样品 B 在 650 K 时显示出最高的塞贝克系数(∼300 μV/K)。另一方面,样品 A 的导电率明显更高(650 K 时为 0.76 × 10⁴ S/m),是其他制备样品的三倍。值得注意的是,样品 A 的功率因数(650 K 时为 0.389 mW/mK2)是样品 B(0.141 mW/mK2)和原始化合物(0.160 mW/mK2)的两倍多。这些研究结果表明,在 Cu 和 S 位置进行双位取代是提高四面体化合物 TE 性能的一种可行策略。
本文章由计算机程序翻译,如有差异,请以英文原文为准。

摘要图片

查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Achieving enhanced power factor using dual substitution at Cu and S sites in tetrahedrites thermoelectric materials Cu12Sb4S13
Thermoelectric (TE) materials-based devices are valuable for translating heat into electricity, but the cost is largely driven by the use of purified metals required for efficient TE performance. This study focuses on tetrahedrite materials, which are cost-effective due to their abundance in copper ore mining waste and status as one of the most widespread sulfosalts on Earth. The research investigates the effects of co-doping and iso-valent doping on the TE properties of p-type tetrahedrite samples, specifically Cu10Mn2Sb4S11Se2 (Sample A) and Cu10MnZnSb₄S11Se2 (Sample B). These samples were synthesized using hot pressing at 773 K and compared with the existing pristine compound (Cu10Mn2Sb4S13). Doping with Mn and Zn (1:1) at the Cu site was found to optimize carrier concentration and enhance phonon scattering, leading to an improved power factor. Additionally, the Se substitution at the S site also introduced band degeneracy, further increasing the power factor. Further, sample B exhibited the highest Seebeck coefficient (∼300 μV/K) at 650 K, in comparison to Sample A (∼225 μV/K) and the pristine compound (∼250 μV/K). On the other hand, Sample A demonstrated significantly higher electrical conductivity (∼0.76 × 10⁴ S/m at 650 K), ∿ three times greater than that of the other prepared samples. Notably, the power factor of Sample A (∼0.389 mW/mK2 at 650 K) was more than twice that of Sample B (∼0.141 mW/mK2) and the pristine compound (∼0.160 mW/mK2). These findings suggest that dual-site substitution at the Cu and S positions presents a promising strategy to augment the TE performance of tetrahedrite compounds.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
Solid State Sciences
Solid State Sciences 化学-无机化学与核化学
CiteScore
6.60
自引率
2.90%
发文量
214
审稿时长
27 days
期刊介绍: Solid State Sciences is the journal for researchers from the broad solid state chemistry and physics community. It publishes key articles on all aspects of solid state synthesis, structure-property relationships, theory and functionalities, in relation with experiments. Key topics for stand-alone papers and special issues: -Novel ways of synthesis, inorganic functional materials, including porous and glassy materials, hybrid organic-inorganic compounds and nanomaterials -Physical properties, emphasizing but not limited to the electrical, magnetical and optical features -Materials related to information technology and energy and environmental sciences. The journal publishes feature articles from experts in the field upon invitation. Solid State Sciences - your gateway to energy-related materials.
期刊最新文献
Study of substrate dependent microstructural properties of sputtered Mo/CZTS heterojunctions using X ray diffraction ZnO/Zn3(PO4)2/CeO2 photocatalysts formed on zinc by plasma electrolytic oxidation Synthesis of Nd2Sn2O7 pyrochlore with different lattice disorder degrees and oxygen vacancy contents Influence of crystalline phase structure of rare earth oxides on active oxygen and basic sites Crystal structures of the R1.33Ni3Ga8 (R = Tb, Ho, Er, Tm, Lu) compounds
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1