Laser powder bed fusion of high-strength crack-free Al7075 alloy with the in-situ formation of TiB2/Al3Ti-reinforced phases and nucleation agents

The existence of solidification cracks caused by columnar grains in precipitation-hardened aluminium alloys limit the applicability of Al7075 components manufactured via laser powder bed fusion (LPBF) additive manufacturing. A novel approach was developed to co-incorporate submicron-sized B and micron-grade Ti6Al4V to eliminate hot cracks and to effectively transform coarse columnar grains into fine equiaxed grains, thus improving the mechanical performance of LPBF-fabricated modified Al7075 material. The grain refinement was mainly attributable to the heterogeneous nucleation promoted by the combination of in-situ-formed L1₂-Al₃Ti and TiB₂ nano-sized phases. After an optimised T6 heat treatment, excellent comprehensive mechanical properties were achieved, with a tensile strength of 460 MPa and an elongation of 13 %. This research provides an efficient and cost-effective path for addressing crack-sensitive metallic materials used for LPBF additive manufacturing processes.