Understanding particle size effect on fast-charging behavior of graphite anode using ultra-thin-layer electrodes

Extreme fast charging (≤15 min) of lithium-ion batteries is highly desirable to accelerate mass-market adoption of electric vehicles. However, significant capacity fading, as well as safety issues due to the lithium plating caused by the fast charging rate, limit its implementation. In this study, we investigated the fast-charging capability of graphite materials with various particle sizes. To eliminate the Li⁺ ion concentration gradient effect across the thickness of the electrode, ultra-thin-layer graphite electrodes were developed to investigate the “real” fast-charging capability of graphite at the particle level. Electrochemical assessments as well as microscopic characterizations revealed that smaller particles exhibited superior fast-charging performance, featuring enhanced capacity reversibility, faster charging rate, and less lithium plating under the same fast-charging conditions. It is shown that small-particle graphite (mean radius of 3.3 μm) could withstand a 4C charge (to 80 % state-of-charge) without plating, with minimal plating occurring at 6C. Thicker particles exhibited plating at lower C-rates. Since the experimental data could not directly explain whether intra-particle diffusion limitations or interfacial reaction limitations dominated the plating mechanism, the pseudo-2-dimensional model was used to evaluate the most likely plating mechanism. The model suggested that particle-level diffusion is the dominant mechanism contributing to plating at high rates. This work provides comprehensive insights into the particle size effects on fast-charging capability, offering a better understanding of fast-charging behavior and valuable guidance for designing optimal electrode architecture for high-rate lithium-ion batteries.