{"title":"新型双固化Composite水泥与氧化锆的粘结性能评价。","authors":"Yue Yan, Huaiqin Zhang, Jiaxue Yang, Chen Chen","doi":"10.3290/j.jad.b2288181","DOIUrl":null,"url":null,"abstract":"<p><strong>Purpose: </strong>To investigate the bond strength and durability of a novel dual-curing composite cement to zirconia under different curing conditions.</p><p><strong>Materials and methods: </strong>Zirconia plates of different thickness (0.5, 1, and 2 mm) were bonded with either a novel dual-curing composite cement (Panavia V5, PV5, Kuraray Noritake) or a traditional one (RelyX Ultimate, RUL, 3M Oral Care; Multilink Automix, MLA, Ivoclar Vivadent), in light-, self-, or dual-curing mode. Bonded specimens were subjected to shear bond strength (SBS) tests after 24 h of water storage or after artificially aging by 20,000 thermal cycles plus 150 days of water storage. The degree of conversion (DC) of the composite cements under different curing conditions was measured by Fourier transform infrared (FTIR) spectroscopy. The irradiance and translucency of the zirconia plates of different thickness were also investigated.</p><p><strong>Results: </strong>The irradiance and translucency of zirconia decreased significantly with increasing thickness (p = 0.00). Both before and after aging, SBS of PV5 in self-curing mode was significantly higher than that of RUL (p = 0.07 before aging and 0.02 after aging) and MLA (p = 0.00 both before and after aging). However, for the three composite cements, light- and dual curing yielding the same SBSs for a constant Y-TZP thickness (p > 0.05). The FTIR analysis showed that, for all three dual-curing composite cements examined in this study, the mean DC values obtained in dual-curing mode were lower than those achieved in light-curing mode (p = 0.00 for PV5, RUL, and MLA). For RUL and MLA, lower mean DC values were obtained in self-curing than dual-curing mode (p = 0.00 for both RUL and MLA), while the DC values of PV5 showed no significant difference between self-curing and dual-curing mode (p = 0.33).</p><p><strong>Conclusion: </strong>When the photoactivation time is 60 s and the thickness of the zirconia restoration is less than 2 mm, it is safe to use the two traditional dual-curing composite cements RUL and MLA and PV5 for bonding zirconia. However, when the light exposure time is insufficient, PV5 provides improved bond strength and durability to zirconia.</p>","PeriodicalId":55604,"journal":{"name":"Journal of Adhesive Dentistry","volume":"23 6","pages":"569-578"},"PeriodicalIF":2.5000,"publicationDate":"2021-12-03","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"3","resultStr":"{\"title\":\"Evaluating the Bonding Performance of a Novel Dual-curing Composite Cement to Zirconia.\",\"authors\":\"Yue Yan, Huaiqin Zhang, Jiaxue Yang, Chen Chen\",\"doi\":\"10.3290/j.jad.b2288181\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p><strong>Purpose: </strong>To investigate the bond strength and durability of a novel dual-curing composite cement to zirconia under different curing conditions.</p><p><strong>Materials and methods: </strong>Zirconia plates of different thickness (0.5, 1, and 2 mm) were bonded with either a novel dual-curing composite cement (Panavia V5, PV5, Kuraray Noritake) or a traditional one (RelyX Ultimate, RUL, 3M Oral Care; Multilink Automix, MLA, Ivoclar Vivadent), in light-, self-, or dual-curing mode. Bonded specimens were subjected to shear bond strength (SBS) tests after 24 h of water storage or after artificially aging by 20,000 thermal cycles plus 150 days of water storage. The degree of conversion (DC) of the composite cements under different curing conditions was measured by Fourier transform infrared (FTIR) spectroscopy. The irradiance and translucency of the zirconia plates of different thickness were also investigated.</p><p><strong>Results: </strong>The irradiance and translucency of zirconia decreased significantly with increasing thickness (p = 0.00). Both before and after aging, SBS of PV5 in self-curing mode was significantly higher than that of RUL (p = 0.07 before aging and 0.02 after aging) and MLA (p = 0.00 both before and after aging). However, for the three composite cements, light- and dual curing yielding the same SBSs for a constant Y-TZP thickness (p > 0.05). The FTIR analysis showed that, for all three dual-curing composite cements examined in this study, the mean DC values obtained in dual-curing mode were lower than those achieved in light-curing mode (p = 0.00 for PV5, RUL, and MLA). For RUL and MLA, lower mean DC values were obtained in self-curing than dual-curing mode (p = 0.00 for both RUL and MLA), while the DC values of PV5 showed no significant difference between self-curing and dual-curing mode (p = 0.33).</p><p><strong>Conclusion: </strong>When the photoactivation time is 60 s and the thickness of the zirconia restoration is less than 2 mm, it is safe to use the two traditional dual-curing composite cements RUL and MLA and PV5 for bonding zirconia. However, when the light exposure time is insufficient, PV5 provides improved bond strength and durability to zirconia.</p>\",\"PeriodicalId\":55604,\"journal\":{\"name\":\"Journal of Adhesive Dentistry\",\"volume\":\"23 6\",\"pages\":\"569-578\"},\"PeriodicalIF\":2.5000,\"publicationDate\":\"2021-12-03\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"3\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Journal of Adhesive Dentistry\",\"FirstCategoryId\":\"3\",\"ListUrlMain\":\"https://doi.org/10.3290/j.jad.b2288181\",\"RegionNum\":3,\"RegionCategory\":\"医学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"DENTISTRY, ORAL SURGERY & MEDICINE\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Adhesive Dentistry","FirstCategoryId":"3","ListUrlMain":"https://doi.org/10.3290/j.jad.b2288181","RegionNum":3,"RegionCategory":"医学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"DENTISTRY, ORAL SURGERY & MEDICINE","Score":null,"Total":0}
Evaluating the Bonding Performance of a Novel Dual-curing Composite Cement to Zirconia.
Purpose: To investigate the bond strength and durability of a novel dual-curing composite cement to zirconia under different curing conditions.
Materials and methods: Zirconia plates of different thickness (0.5, 1, and 2 mm) were bonded with either a novel dual-curing composite cement (Panavia V5, PV5, Kuraray Noritake) or a traditional one (RelyX Ultimate, RUL, 3M Oral Care; Multilink Automix, MLA, Ivoclar Vivadent), in light-, self-, or dual-curing mode. Bonded specimens were subjected to shear bond strength (SBS) tests after 24 h of water storage or after artificially aging by 20,000 thermal cycles plus 150 days of water storage. The degree of conversion (DC) of the composite cements under different curing conditions was measured by Fourier transform infrared (FTIR) spectroscopy. The irradiance and translucency of the zirconia plates of different thickness were also investigated.
Results: The irradiance and translucency of zirconia decreased significantly with increasing thickness (p = 0.00). Both before and after aging, SBS of PV5 in self-curing mode was significantly higher than that of RUL (p = 0.07 before aging and 0.02 after aging) and MLA (p = 0.00 both before and after aging). However, for the three composite cements, light- and dual curing yielding the same SBSs for a constant Y-TZP thickness (p > 0.05). The FTIR analysis showed that, for all three dual-curing composite cements examined in this study, the mean DC values obtained in dual-curing mode were lower than those achieved in light-curing mode (p = 0.00 for PV5, RUL, and MLA). For RUL and MLA, lower mean DC values were obtained in self-curing than dual-curing mode (p = 0.00 for both RUL and MLA), while the DC values of PV5 showed no significant difference between self-curing and dual-curing mode (p = 0.33).
Conclusion: When the photoactivation time is 60 s and the thickness of the zirconia restoration is less than 2 mm, it is safe to use the two traditional dual-curing composite cements RUL and MLA and PV5 for bonding zirconia. However, when the light exposure time is insufficient, PV5 provides improved bond strength and durability to zirconia.
期刊介绍：
New materials and applications for adhesion are profoundly changing the way dentistry is delivered. Bonding techniques, which have long been restricted to the tooth hard tissues, enamel, and dentin, have obvious applications in operative and preventive dentistry, as well as in esthetic and pediatric dentistry, prosthodontics, and orthodontics. The current development of adhesive techniques for soft tissues and slow-releasing agents will expand applications to include periodontics and oral surgery. Scientifically sound, peer-reviewed articles explore the latest innovations in these emerging fields.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们