Multifunctional polyethylene imine hybrids decorated by silica bioactive glass with enhanced mechanical properties, antibacterial, and osteogenesis for bone repair

Inorganic/organic hybrids and bioactive glasses demonstrate promising potential as bone substitute biomaterials. A sol-gel hybrid consisting of silica bioactive glass and biodegradable polymer can combine the high bioactivity of a glass with the toughness of a polymer. In this study, multifunctional hybrids with a combination of organic-inorganic hybrid structure class II consisting of polyethyleneimine (PEI) generation 4 (G4) and bioactive glass with enhanced mechanical properties, mineralization, antibacterial, and osteogenesis activities were synthesized by the sol-gel method. Glycidoxypropyl) trimethoxysilane (GPTMS) with different concentrations was used as a covalent bonding agent between PEI polymer and bioactive glass. The effect of GPTMS content was assessed in the presence and absence of calcium in the hybrid structures in terms of morphology, wettability, mechanical properties, antibacterial activity, cell viability, and in vitro osteogenic differentiation properties. By increasing the amount of GPTMS, the compressive strength increased from 1.95 MPa to 2.34 MPa, which was comparable to human trabecular bone. All the hybrids presented antibacterial activity against Staphylococcus aureus, forming an inhibition zone of 13–16 mm. An increase in cell viability of 82.22% in PSCaG90 was obtained after 1 day of MG-63 cell culture. Alkaline phosphatase expression and mineralization of MG-63 cells increased in the PSCaG90 hybrid in the absence of an osteogenic medium compared to PSG60 and PSG90. The PSCaG90 hybrid indicated considerable in vitro osteogenic capacity in the absence of a differentiation medium, expressing high levels of bone-specific proteins including collagen I (COL1A1), Runt-related transcription factor 2 (RUNX2), osteopontin (OPN), and osteocalcin (OCN), compared to calcium-free hybrids. Overall, our results suggest that the presence of calcium in the PSCaG90 leads to a significant increase in osteogenic differentiation of MG-63 cells even in the absence of differentiation medium, which suggests these hybrid structures with multifunctional properties as promising candidates for bone repair.