Efeito Biomodificador de Diferentes Agentes de Ligações Cruzadas nas Propriedades Mecânicas do Colágeno Dentinário

Objective: to evaluate the biomodifying effect of cross-linking agents on the mechanical properties of the teeth. Material and Methods: this is an in vitro laboratory study, in which 18 bars of dentin were made from extracted, caries-free human third molars. The samples were demineralized in 10% phosphoric acid for 5 hours, randomly distributed in different groups and kept in their pre-treatment solutions: distilled water (AD), Proanthocyanidin at 6.5% (PAC6.5) and Cardanol at 6.5% (CAR6.5) for periods of 1 hour. Three-point bending tests were performed to obtain the modulus of elasticity (ME) and mass modification (MM). They were submitted to the Kolmogorov-Smirnoff test followed by the Kruskal-Wallis’ test and the Tukey’s post-test for mass modification, and Kruskal-Wallis’ test after a Dunn’s test for difference in the modulus of elasticity(p <0.05). Results: the values selected in the ME show possible statistical changes in all groups tested, when compared to the negative control (p<0.001), as well as the mass variation. Data were shown in the average values between the groups tested (p = 0.012). Conclusion: The use of PAC6.5 will improve the mechanical properties of the collection