{"title":"液体火箭发动机用S-07钢断裂机理及失效准则","authors":"Yushan Gao, Wei Jiang, S. Huo","doi":"10.1108/mmms-11-2022-0257","DOIUrl":null,"url":null,"abstract":"PurposeThe fracture mechanism of S-07 steel was investigated by observing the fracture surface of the specimens with scanning electron microscope (SEM). Furthermore, the overall elastic–plastic behaviors and the stress state evolution during the loading procedure of all specimens were simulated by FE analysis to obtain the local strain at crack nucleated location and the average triaxiality of each type of specimen.Design/methodology/approachThree types of tests under various stress states were performed to study the ductile fracture characteristics of S-07 high strength steel in quasi-static condition.FindingsUnder tensile and torsion loading conditions, S-07 steel exhibits two distinctive rupture mechanisms: the growth and internal necking of voids governs the rupture mechanism in tension dominated loading mode, while the change of void shape and internal shearing in the ligaments between voids dominants for shear conditions.Originality/valueThe failure criterion for S-07 steel considering the influence of the triaxial stress state was established.","PeriodicalId":46760,"journal":{"name":"Multidiscipline Modeling in Materials and Structures","volume":" ","pages":""},"PeriodicalIF":1.7000,"publicationDate":"2023-03-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Fracture mechanism and failure criterion of S-07 steel for liquid rocket engine\",\"authors\":\"Yushan Gao, Wei Jiang, S. Huo\",\"doi\":\"10.1108/mmms-11-2022-0257\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"PurposeThe fracture mechanism of S-07 steel was investigated by observing the fracture surface of the specimens with scanning electron microscope (SEM). Furthermore, the overall elastic–plastic behaviors and the stress state evolution during the loading procedure of all specimens were simulated by FE analysis to obtain the local strain at crack nucleated location and the average triaxiality of each type of specimen.Design/methodology/approachThree types of tests under various stress states were performed to study the ductile fracture characteristics of S-07 high strength steel in quasi-static condition.FindingsUnder tensile and torsion loading conditions, S-07 steel exhibits two distinctive rupture mechanisms: the growth and internal necking of voids governs the rupture mechanism in tension dominated loading mode, while the change of void shape and internal shearing in the ligaments between voids dominants for shear conditions.Originality/valueThe failure criterion for S-07 steel considering the influence of the triaxial stress state was established.\",\"PeriodicalId\":46760,\"journal\":{\"name\":\"Multidiscipline Modeling in Materials and Structures\",\"volume\":\" \",\"pages\":\"\"},\"PeriodicalIF\":1.7000,\"publicationDate\":\"2023-03-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Multidiscipline Modeling in Materials and Structures\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.1108/mmms-11-2022-0257\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q3\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Multidiscipline Modeling in Materials and Structures","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1108/mmms-11-2022-0257","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
Fracture mechanism and failure criterion of S-07 steel for liquid rocket engine
PurposeThe fracture mechanism of S-07 steel was investigated by observing the fracture surface of the specimens with scanning electron microscope (SEM). Furthermore, the overall elastic–plastic behaviors and the stress state evolution during the loading procedure of all specimens were simulated by FE analysis to obtain the local strain at crack nucleated location and the average triaxiality of each type of specimen.Design/methodology/approachThree types of tests under various stress states were performed to study the ductile fracture characteristics of S-07 high strength steel in quasi-static condition.FindingsUnder tensile and torsion loading conditions, S-07 steel exhibits two distinctive rupture mechanisms: the growth and internal necking of voids governs the rupture mechanism in tension dominated loading mode, while the change of void shape and internal shearing in the ligaments between voids dominants for shear conditions.Originality/valueThe failure criterion for S-07 steel considering the influence of the triaxial stress state was established.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们