耐超高温RTM双马来酰亚胺树脂的固化行为与性能

IF 1.8 4区 化学 Q3 POLYMER SCIENCE High Performance Polymers Pub Date : 2022-12-22 DOI:10.1177/09540083221146926
X. Xiong, Jianxin Ai, R. Ren, Jing Wang, Guiyang Li
{"title":"耐超高温RTM双马来酰亚胺树脂的固化行为与性能","authors":"X. Xiong, Jianxin Ai, R. Ren, Jing Wang, Guiyang Li","doi":"10.1177/09540083221146926","DOIUrl":null,"url":null,"abstract":"The properties of a RTM bismaleimide resin with low viscosity and ultra-high temperature resistance were systematically investigated, including its curing kinetics and rheological properties, and the thermal and mechanical properties of its cured resins. The thermal curing kinetics was investigated by differential scanning calorimetry (DSC) method with multiple heating rates. DSC curves display a cure regime in the temperature range of 150∼300°C and the exothermic peaks shift from 194°C to 231°C with heating rate. The apparent activation energy of curing reaction is calculated as 78.2 kJ/mol. The rheological properties were studied in terms of the changes of the non-isothermal and isothermal viscosity tested using a rotary viscometer. The test results show that the RTM resin has a wide molding temperature window from 90°C to 200°C and long molding time at 110°C for 275 min with a flow viscosity less than 1000 mPas. Dual-Arrhenius model was established to predict the viscosity characteristics at different constant temperatures, showing a good agreement with the experimental data. Four curing cycles were designed to obtain cured networks with different microstructures, and the thermal and mechanical properties of the cured resins suffered from various curing cycles were characterized by dynamic mechanical analysis (DMA) and universal material testing machine. The results exhibit that the cured product has a ultra-high glass transition temperature of 373.5°C and larger flexural strength of 145.4 MPa after post-curing at 250°C for 10 h.","PeriodicalId":12932,"journal":{"name":"High Performance Polymers","volume":"35 1","pages":"469 - 479"},"PeriodicalIF":1.8000,"publicationDate":"2022-12-22","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Curing behavior and properties of ultra-high temperature resistant RTM bismaleimide resin\",\"authors\":\"X. Xiong, Jianxin Ai, R. Ren, Jing Wang, Guiyang Li\",\"doi\":\"10.1177/09540083221146926\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The properties of a RTM bismaleimide resin with low viscosity and ultra-high temperature resistance were systematically investigated, including its curing kinetics and rheological properties, and the thermal and mechanical properties of its cured resins. The thermal curing kinetics was investigated by differential scanning calorimetry (DSC) method with multiple heating rates. DSC curves display a cure regime in the temperature range of 150∼300°C and the exothermic peaks shift from 194°C to 231°C with heating rate. The apparent activation energy of curing reaction is calculated as 78.2 kJ/mol. The rheological properties were studied in terms of the changes of the non-isothermal and isothermal viscosity tested using a rotary viscometer. The test results show that the RTM resin has a wide molding temperature window from 90°C to 200°C and long molding time at 110°C for 275 min with a flow viscosity less than 1000 mPas. Dual-Arrhenius model was established to predict the viscosity characteristics at different constant temperatures, showing a good agreement with the experimental data. Four curing cycles were designed to obtain cured networks with different microstructures, and the thermal and mechanical properties of the cured resins suffered from various curing cycles were characterized by dynamic mechanical analysis (DMA) and universal material testing machine. The results exhibit that the cured product has a ultra-high glass transition temperature of 373.5°C and larger flexural strength of 145.4 MPa after post-curing at 250°C for 10 h.\",\"PeriodicalId\":12932,\"journal\":{\"name\":\"High Performance Polymers\",\"volume\":\"35 1\",\"pages\":\"469 - 479\"},\"PeriodicalIF\":1.8000,\"publicationDate\":\"2022-12-22\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"High Performance Polymers\",\"FirstCategoryId\":\"92\",\"ListUrlMain\":\"https://doi.org/10.1177/09540083221146926\",\"RegionNum\":4,\"RegionCategory\":\"化学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q3\",\"JCRName\":\"POLYMER SCIENCE\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"High Performance Polymers","FirstCategoryId":"92","ListUrlMain":"https://doi.org/10.1177/09540083221146926","RegionNum":4,"RegionCategory":"化学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"POLYMER SCIENCE","Score":null,"Total":0}
引用次数: 0

摘要

系统地研究了一种低粘度、耐超高温的RTM双马来酰亚胺树脂的固化动力学和流变性能,以及固化树脂的热力学性能。采用差示扫描量热法(DSC)研究了不同加热速率下的热固化动力学。DSC曲线在150 ~ 300℃的温度范围内呈现固化状态,放热峰随升温速率从194℃移至231℃。固化反应的表观活化能为78.2 kJ/mol。用旋转粘度计对其非等温粘度和等温粘度的变化进行了研究。试验结果表明,RTM树脂在90℃~ 200℃范围内具有较宽的成型温度窗,在110℃下成型275 min时间长,流动粘度小于1000 mpa。建立了双arrhenius模型,对不同恒温条件下的粘度特性进行了预测,结果与实验数据吻合较好。设计了4个固化循环,获得了具有不同微观组织的固化网络,并利用动态力学分析(DMA)和万能材料试验机对不同固化循环下固化树脂的热力学性能进行了表征。结果表明,在250℃下固化10 h后,固化产物具有373.5℃的超高玻璃化转变温度和145.4 MPa的较大抗弯强度。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Curing behavior and properties of ultra-high temperature resistant RTM bismaleimide resin
The properties of a RTM bismaleimide resin with low viscosity and ultra-high temperature resistance were systematically investigated, including its curing kinetics and rheological properties, and the thermal and mechanical properties of its cured resins. The thermal curing kinetics was investigated by differential scanning calorimetry (DSC) method with multiple heating rates. DSC curves display a cure regime in the temperature range of 150∼300°C and the exothermic peaks shift from 194°C to 231°C with heating rate. The apparent activation energy of curing reaction is calculated as 78.2 kJ/mol. The rheological properties were studied in terms of the changes of the non-isothermal and isothermal viscosity tested using a rotary viscometer. The test results show that the RTM resin has a wide molding temperature window from 90°C to 200°C and long molding time at 110°C for 275 min with a flow viscosity less than 1000 mPas. Dual-Arrhenius model was established to predict the viscosity characteristics at different constant temperatures, showing a good agreement with the experimental data. Four curing cycles were designed to obtain cured networks with different microstructures, and the thermal and mechanical properties of the cured resins suffered from various curing cycles were characterized by dynamic mechanical analysis (DMA) and universal material testing machine. The results exhibit that the cured product has a ultra-high glass transition temperature of 373.5°C and larger flexural strength of 145.4 MPa after post-curing at 250°C for 10 h.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
High Performance Polymers
High Performance Polymers 化学-高分子科学
CiteScore
4.20
自引率
14.30%
发文量
106
审稿时长
1.2 months
期刊介绍: Health Services Management Research (HSMR) is an authoritative international peer-reviewed journal which publishes theoretically and empirically rigorous research on questions of enduring interest to health-care organizations and systems throughout the world. Examining the real issues confronting health services management, it provides an independent view and cutting edge evidence-based research to guide policy-making and management decision-making. HSMR aims to be a forum serving an international community of academics and researchers on the one hand and healthcare managers, executives, policymakers and clinicians and all health professionals on the other. HSMR wants to make a substantial contribution to both research and managerial practice, with particular emphasis placed on publishing studies which offer actionable findings and on promoting knowledge mobilisation toward theoretical advances. All papers are expected to be of interest and relevance to an international audience. HSMR aims at enhance communication between academics and practitioners concerned with developing, implementing, and analysing health management issues, reforms and innovations primarily in European health systems and in all countries with developed health systems. Papers can report research undertaken in a single country, but they need to locate and explain their findings in an international context, and in international literature.
期刊最新文献
The fabrication of polyimide-based tunable ternary memristors doped with Ni-Co coated carbon composite nanofibers Analysis of the impact of exfoliated graphene oxide on the mechanical performance and in-plane fracture resistance of epoxy-based nanocomposite Preparation of halogen-free flame retardant curing agent and its application in epoxy resin Bio-based phthalonitrile resin derived from quercetin as a sustainable molecular scaffold: Synthesis, curing reaction and comparison with petroleum-based counterparts Copolymerization of novel self-promoted curing phthalonitrile with epoxy resin and its thermal property
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1