The Effect of Recycled Citrogypsum as a Supplementary Mineral Additive on the Physical and Mechanical Performance of Granulated Blast Furnace Slag-Based Alkali-Activated Binders

In the last decades, gypsum-bearing industrial wastes become one of the common globally produced industrial and domestic wastes that are currently recycled and further utilized. In this study, the gypsum-bearing waste citrogypsum was used as a Ca2+-containing component to modify the properties of alkali-activated cement (AAC) based on granulated blast-furnace slag (GBFS). Citrogypsum was used in different AAC mixes activated with three different alkaline components: Na2CO3, NaOH, and Na2SiO3. Laser granulometry was applied to assess the granulometric characteristics of citrogypsum and GBFS. Specific gravity (SG), compressive strength, and water resistance were tested to evaluate the effect of citrogypsum on the physical and strength performance of AAC. Experimental results obtained over 4-day to 28-day time periods for the studied AACs showed that the addition of citrogypsum had a detrimental effect on the properties of AAC mixes, where decreases in compressive strength between 1 and 100%, decreases in specific gravity between 4 and 30%, and decreases in water resistance between 12 and 100% were observed. It was determined that AAC mixes modified with citrogypsum cured in ambient conditions had compressive strength values 61% to 90% lower than those cured in hydrothermal conditions. In terms of strength performance, specific gravity and water resistance, citrogypsum showed the greatest effect on AAC mixes activated with NaOH, and to a lesser extent, on mixes activated with Na2CO3. The highest water resistance value of 0.77 was observed for the AAC mixes activated with Na2CO3 cured in ambient conditions, and when cured in hydrothermal conditions, the highest water resistance reached up to 0.84 for the AAC mixes activated with NaOH. It was observed that the type of alkaline activator and curing conditions are both crucial factors that govern the response of citrogypsum as a supplementary mineral additive in GBFS-based AAC mixes in regard to compressive strength, specific gravity and water resistance.