Influence of Acid Etching on Bond Strength Between Feldspathic Ceramics and Resin Cement

Objective: analyze the influence of bond strength between resin cement and feldspathic ceramics using different concentrations and application times of hydrofluoric acid (HF). Materials and Methods: 18 feldspathic ceramic discs (Ø10mm 2mm thickness) were made through the incremental technique, which were included in acrylic resin and regularized with silicon carbide sandpaper with granulations of 600, 1200 and 2000 through a polishing machine with a speed of 600 rpm. Soon after, they were immersed in distilled water for 10 minutes in an ultrasonic bath. All specimens were conditioned with HF and silanized. Four cement cylinders were made on each specimen (n=12), manufactured with Relyx ARC resin cement. After that, it was divided into six groups according to the surface treatment protocol: G1 (5% 40s); G2 (5% 60s); G3 (5% 80s); G4 (10% 40s); G5 (10% 60s) e G6 (10% 80s). The specimens were subjected to the Microshear Test, with vertical force at a speed of 0.5 mm min on the specimen. The microshear bond strength was calculated and expressed in Megapascal (MPa). The data were submitted to two-way analysis of variance (ANOVA) and Tukey’s test for multiple comparisons, with a significance level of 5%. Results: when the concentration of HF was analyzed, there were no statistical differences (p>0.05). In the comparison of application times, G3 (5% 80s) and G6 (10% 80s) obtained higher results of microshear resistance than the other groups. Conclusion: The different concentrations of HF did not influence the bond strength between feldspathic ceramics and resin cement. However, the increase in the time of HF conditioning affected in the bond strength.