{"title":"硫酸化剂与 HOCl 涂膜层脱蛋白结合使用可提高一步法自酸蚀粘合剂的牙本质粘合耐久性。","authors":"Kittisak Sanon, Antonin Tichy, Ornnicha Thanatvarakorn, Taweesak Prasansuttiporn, Kazuhide Yonekura, Keiichi Hosaka, Masayuki Otsuki, Masatoshi Nakajima","doi":"10.3290/j.jad.b2920099","DOIUrl":null,"url":null,"abstract":"<p><strong>Purpose: </strong>To evaluate the effect of a sulfinate agent on the bonding durability of one-step self-etch adhesives (1-SEAs) to smear-layer-covered dentin deproteinized with hypochlorous acid (HOCl).</p><p><strong>Materials and methods: </strong>Human coronal dentin disks with a standardized smear layer were deproteinized with 100 ppm HOCl solution for 0 s (control), 15 s or 30 s. After rinsing with water for 30 s and air drying, half of the specimens were treated with a sulfinate agent (Scotchbond Universal Dual Cure Activator; SDA) prior to the application of a 1-SEA (Bond Force II [Tokuyama Dental] or Clearfil Universal Bond Quick [Kuraray Noritake]). Microtensile bond strength (µTBS) was measured after 24 h or 10,000 thermal cycles (TC). The data were analyzed by three-way ANOVA with Tukey's post-hoc tests and t-tests at the 0.05 significance level.</p><p><strong>Results: </strong>The 24-h µTBS of both adhesives increased statistically significantly with the HOCl pretreatment for 15 s or 30 s (p < 0.05), but it was not statistically significantly affected by the application of SDA (p > 0.05). However, after TC, the groups treated with the combination of HOCl and SDA maintained their µTBS (p > 0.05), as opposed to untreated dentin and dentin treated with either HOCl or SDA, whose µTBS decreased significantly (p < 0.05).</p><p><strong>Conclusion: </strong>The application of the sulfinate agent did not statistically significantly affect the immediate bond strength of 1-SEAs, and it could not prevent a significant decrease in the bond strength to untreated dentin after thermocycling. However, the sulfinate agent significantly improved the bonding durability of 1-SEAs to HOCl smear-layer deproteinized dentin.</p>","PeriodicalId":94234,"journal":{"name":"The journal of adhesive dentistry","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2022-04-14","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Application of Sulfinate Agent in Conjunction with HOCl Smear-Layer Deproteinization Improves Dentin Bonding Durability of One-step Self-etch Adhesives.\",\"authors\":\"Kittisak Sanon, Antonin Tichy, Ornnicha Thanatvarakorn, Taweesak Prasansuttiporn, Kazuhide Yonekura, Keiichi Hosaka, Masayuki Otsuki, Masatoshi Nakajima\",\"doi\":\"10.3290/j.jad.b2920099\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p><strong>Purpose: </strong>To evaluate the effect of a sulfinate agent on the bonding durability of one-step self-etch adhesives (1-SEAs) to smear-layer-covered dentin deproteinized with hypochlorous acid (HOCl).</p><p><strong>Materials and methods: </strong>Human coronal dentin disks with a standardized smear layer were deproteinized with 100 ppm HOCl solution for 0 s (control), 15 s or 30 s. After rinsing with water for 30 s and air drying, half of the specimens were treated with a sulfinate agent (Scotchbond Universal Dual Cure Activator; SDA) prior to the application of a 1-SEA (Bond Force II [Tokuyama Dental] or Clearfil Universal Bond Quick [Kuraray Noritake]). Microtensile bond strength (µTBS) was measured after 24 h or 10,000 thermal cycles (TC). The data were analyzed by three-way ANOVA with Tukey's post-hoc tests and t-tests at the 0.05 significance level.</p><p><strong>Results: </strong>The 24-h µTBS of both adhesives increased statistically significantly with the HOCl pretreatment for 15 s or 30 s (p < 0.05), but it was not statistically significantly affected by the application of SDA (p > 0.05). However, after TC, the groups treated with the combination of HOCl and SDA maintained their µTBS (p > 0.05), as opposed to untreated dentin and dentin treated with either HOCl or SDA, whose µTBS decreased significantly (p < 0.05).</p><p><strong>Conclusion: </strong>The application of the sulfinate agent did not statistically significantly affect the immediate bond strength of 1-SEAs, and it could not prevent a significant decrease in the bond strength to untreated dentin after thermocycling. However, the sulfinate agent significantly improved the bonding durability of 1-SEAs to HOCl smear-layer deproteinized dentin.</p>\",\"PeriodicalId\":94234,\"journal\":{\"name\":\"The journal of adhesive dentistry\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2022-04-14\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"The journal of adhesive dentistry\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.3290/j.jad.b2920099\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"The journal of adhesive dentistry","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.3290/j.jad.b2920099","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Application of Sulfinate Agent in Conjunction with HOCl Smear-Layer Deproteinization Improves Dentin Bonding Durability of One-step Self-etch Adhesives.
Purpose: To evaluate the effect of a sulfinate agent on the bonding durability of one-step self-etch adhesives (1-SEAs) to smear-layer-covered dentin deproteinized with hypochlorous acid (HOCl).
Materials and methods: Human coronal dentin disks with a standardized smear layer were deproteinized with 100 ppm HOCl solution for 0 s (control), 15 s or 30 s. After rinsing with water for 30 s and air drying, half of the specimens were treated with a sulfinate agent (Scotchbond Universal Dual Cure Activator; SDA) prior to the application of a 1-SEA (Bond Force II [Tokuyama Dental] or Clearfil Universal Bond Quick [Kuraray Noritake]). Microtensile bond strength (µTBS) was measured after 24 h or 10,000 thermal cycles (TC). The data were analyzed by three-way ANOVA with Tukey's post-hoc tests and t-tests at the 0.05 significance level.
Results: The 24-h µTBS of both adhesives increased statistically significantly with the HOCl pretreatment for 15 s or 30 s (p < 0.05), but it was not statistically significantly affected by the application of SDA (p > 0.05). However, after TC, the groups treated with the combination of HOCl and SDA maintained their µTBS (p > 0.05), as opposed to untreated dentin and dentin treated with either HOCl or SDA, whose µTBS decreased significantly (p < 0.05).
Conclusion: The application of the sulfinate agent did not statistically significantly affect the immediate bond strength of 1-SEAs, and it could not prevent a significant decrease in the bond strength to untreated dentin after thermocycling. However, the sulfinate agent significantly improved the bonding durability of 1-SEAs to HOCl smear-layer deproteinized dentin.