带表面裂纹钢板的拉伸断裂破坏研究

IF 0.6 4区工程技术 Q4 MECHANICS Journal of Theoretical and Applied Mechanics Pub Date : 2023-04-28 DOI:10.15632/jtam-pl/162991

Zhewen Chong, Jing Tao, Yuehui Xie, Dongrong Wu, Tao Li

{"title":"带表面裂纹钢板的拉伸断裂破坏研究","authors":"Zhewen Chong, Jing Tao, Yuehui Xie, Dongrong Wu, Tao Li","doi":"10.15632/jtam-pl/162991","DOIUrl":null,"url":null,"abstract":"In order to study the eﬀect of diﬀerent surface crack parameters on the fracture failure of steel plate, the model was established by FEM. The results showed that the edge surface crack has the greatest inﬂuence on the fracture failure of the steel plate, and for non-edge surface cracks, the central surface crack has the greatest inﬂuence on the fracture failure of the steel plate. The larger the a/t and the smaller the a/c , the easier the steel plate fracture failure occurs. The a/c has a certain inﬂuence on the variation law of K and the position where K max appears.","PeriodicalId":49980,"journal":{"name":"Journal of Theoretical and Applied Mechanics","volume":"167 1","pages":""},"PeriodicalIF":0.6000,"publicationDate":"2023-04-28","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"2","resultStr":"{\"title\":\"Study on tensile fracture failure of a steel plate with a surface crack\",\"authors\":\"Zhewen Chong, Jing Tao, Yuehui Xie, Dongrong Wu, Tao Li\",\"doi\":\"10.15632/jtam-pl/162991\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"In order to study the eﬀect of diﬀerent surface crack parameters on the fracture failure of steel plate, the model was established by FEM. The results showed that the edge surface crack has the greatest inﬂuence on the fracture failure of the steel plate, and for non-edge surface cracks, the central surface crack has the greatest inﬂuence on the fracture failure of the steel plate. The larger the a/t and the smaller the a/c , the easier the steel plate fracture failure occurs. The a/c has a certain inﬂuence on the variation law of K and the position where K max appears.\",\"PeriodicalId\":49980,\"journal\":{\"name\":\"Journal of Theoretical and Applied Mechanics\",\"volume\":\"167 1\",\"pages\":\"\"},\"PeriodicalIF\":0.6000,\"publicationDate\":\"2023-04-28\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"2\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Journal of Theoretical and Applied Mechanics\",\"FirstCategoryId\":\"5\",\"ListUrlMain\":\"https://doi.org/10.15632/jtam-pl/162991\",\"RegionNum\":4,\"RegionCategory\":\"工程技术\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"MECHANICS\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Theoretical and Applied Mechanics","FirstCategoryId":"5","ListUrlMain":"https://doi.org/10.15632/jtam-pl/162991","RegionNum":4,"RegionCategory":"工程技术","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MECHANICS","Score":null,"Total":0}

引用次数: 2

摘要

为了研究不同表面裂纹参数对钢板断裂破坏的影响，采用有限元方法建立了钢板断裂破坏模型。结果表明:边缘表面裂纹对钢板断裂破坏的影响最大，对于非边缘表面裂纹，中心表面裂纹对钢板断裂破坏的影响最大。a/t越大，a/c越小，钢板越容易发生断裂破坏。a/c对K的变化规律和K最大值出现的位置有一定的影响。

本文章由计算机程序翻译，如有差异，请以英文原文为准。

查看原文

微信好友朋友圈 QQ好友复制链接

本刊更多论文

Study on tensile fracture failure of a steel plate with a surface crack

In order to study the eﬀect of diﬀerent surface crack parameters on the fracture failure of steel plate, the model was established by FEM. The results showed that the edge surface crack has the greatest inﬂuence on the fracture failure of the steel plate, and for non-edge surface cracks, the central surface crack has the greatest inﬂuence on the fracture failure of the steel plate. The larger the a/t and the smaller the a/c , the easier the steel plate fracture failure occurs. The a/c has a certain inﬂuence on the variation law of K and the position where K max appears.

求助全文

通过发布文献求助，成功后即可免费获取论文全文。去求助

来源期刊

Journal of Theoretical and Applied Mechanics 物理-力学

CiteScore

1.40

自引率

14.30%

发文量

审稿时长

6 months

期刊介绍： The scope of JTAM contains: - solid mechanics - fluid mechanics - fluid structures interactions - stability and vibrations systems - robotic and control systems - mechanics of materials - dynamics of machines, vehicles and flying structures - inteligent systems - nanomechanics - biomechanics - computational mechanics