Structure and some properties of methacrylonitrile/divinylbenzene macroporous copolymers

Copolymers of methacrylonitrile (MAN) and divinylbenzene (DVB) of different crosslinking degree between 6–50 wt.-% DVB were obtained by suspension polymerization of monomers in the presence of a diluent (1 : 1, v/v), i.e. a mixture of toluene with tetradecane (9 : 1, v/v). Porosity of the copolymers (MAN/DVB) has been found to fall in the range 48–57.3%. Specific surface area of the copolymers increased in the range of mesopores with the increasing crosslinking degree. Sorption properties of the copolymers towards aqueous phenol solution are similar to those of acrylonitrile-DVB copolymers. MAN/DVB copolymers display rather poor thermal stability (low residue) what indicates that thermally initiated cyclization of nitrile groups can not take place and the influence of depolymerization may be significant. Copolymere aus Methacrylnitril (MAN) und Divinylbenzol (DVB) mit unterschiedlichen Vernetzergehalten zwischen 6 und 50 Gew.-% DVB wurden durch Suspensions-polymerisation in Gegenwart eines Losungsmittelgemisches (1 : 1, v/v) aus Toluol und Tetradecan (9 : 1, v/v) hergestellt. Die Porositat der Copolymeren (MAN/DVB) lag zwischen 48 und 57,3%. Die spezifische Oberflache der Copolymeren nahm mit steigendem Vernetzungsgrad zu. Die Sorptionseigenschaften fur eine wasserige Phenollosung ahneln denen von Acrylnitril/DVB-Copolymeren. Die thermische Stabilitat der MAN/DVB-Copolymeren ist vergleichsweise schlecht (geringer Ruckstand), wahrscheinlich dadurch bedingt, das die Nitrilgruppen nicht thermisch cyclisiert werden konnen und die Depolymerisation einen merklichen Einflus hat.