{"title":"电弧侵蚀在受电弓-接触网系统碳带/铜接触线严重磨损中的作用","authors":"T. Ding, G. Chen, S. Xiao, L. Xie, Q. Zeng","doi":"10.1109/CCIENG.2011.6008123","DOIUrl":null,"url":null,"abstract":"Experimental tests on friction and wear behavior of copper contact line/carbon strip were carried out under the conditions of different electric current on a pin-on-disc tester. During testing, the coefficient of friction and wear rate were recorded and arc discharge phenomenon was observed. The result indicated that friction coefficient decrease with increase of electric current intensity due to the lubrication role of electric current. As the electric current increased, wear volume distinctly increased due arc discharge ablation. By analysis of SEM micrograph and EDX spectrum on wear surface of carbon strip, it is known that arc erosion, oxidative wear and metal melting are dominant with electric current and abrasive wear and adhesive wear are dominant without electric current.","PeriodicalId":6316,"journal":{"name":"2011 IEEE 2nd International Conference on Computing, Control and Industrial Engineering","volume":"6 1","pages":"297-299"},"PeriodicalIF":0.0000,"publicationDate":"2011-09-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":"{\"title\":\"The role of the arc erosion in sever wear of carbon strip/copper contact wire in pantograph-catenry system\",\"authors\":\"T. Ding, G. Chen, S. Xiao, L. Xie, Q. Zeng\",\"doi\":\"10.1109/CCIENG.2011.6008123\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Experimental tests on friction and wear behavior of copper contact line/carbon strip were carried out under the conditions of different electric current on a pin-on-disc tester. During testing, the coefficient of friction and wear rate were recorded and arc discharge phenomenon was observed. The result indicated that friction coefficient decrease with increase of electric current intensity due to the lubrication role of electric current. As the electric current increased, wear volume distinctly increased due arc discharge ablation. By analysis of SEM micrograph and EDX spectrum on wear surface of carbon strip, it is known that arc erosion, oxidative wear and metal melting are dominant with electric current and abrasive wear and adhesive wear are dominant without electric current.\",\"PeriodicalId\":6316,\"journal\":{\"name\":\"2011 IEEE 2nd International Conference on Computing, Control and Industrial Engineering\",\"volume\":\"6 1\",\"pages\":\"297-299\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2011-09-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"1\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"2011 IEEE 2nd International Conference on Computing, Control and Industrial Engineering\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1109/CCIENG.2011.6008123\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"2011 IEEE 2nd International Conference on Computing, Control and Industrial Engineering","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1109/CCIENG.2011.6008123","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
The role of the arc erosion in sever wear of carbon strip/copper contact wire in pantograph-catenry system
Experimental tests on friction and wear behavior of copper contact line/carbon strip were carried out under the conditions of different electric current on a pin-on-disc tester. During testing, the coefficient of friction and wear rate were recorded and arc discharge phenomenon was observed. The result indicated that friction coefficient decrease with increase of electric current intensity due to the lubrication role of electric current. As the electric current increased, wear volume distinctly increased due arc discharge ablation. By analysis of SEM micrograph and EDX spectrum on wear surface of carbon strip, it is known that arc erosion, oxidative wear and metal melting are dominant with electric current and abrasive wear and adhesive wear are dominant without electric current.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们