H. A. Youssef, M. Aziz, F. Yoshii, K. Makuuchi, A. A. Miligy
{"title":"苯乙烯含量和硬脂酸锌对辐射硫化丁苯橡胶(SBR)力学性能的影响","authors":"H. A. Youssef, M. Aziz, F. Yoshii, K. Makuuchi, A. A. Miligy","doi":"10.1002/APMC.1994.052180102","DOIUrl":null,"url":null,"abstract":"The effect of styrene content on the properties of electron irradiation-vulcanized SBR loaded with carbon black was pronounced only at low irradiation doses where the crosslinking densities were not so high. At high doses, no effect was observed especially for SBR containing ZnO. It was also observed that ZnO (3 phr) increased the tensile strength of SBR containing 23.5 wt.-% styrene by 20% at 20 kGy irradiation dose, compared to 5% at higher doses for SBR containing 46 wt.-% styrene. However, the increase in tensile strength by ZnO for loaded SBR (23.5%) was almost 17% at all irradiation doses. Besides, tear strength, abrasion resistance and elongation at break were remarkably improved. The high efficiency of ZnO toward SBR (23.5%) may be attributed to the higher butadiene content. The behavior of SBR (46%) at 20 kGy was surprising, since both tensile strength and elongation at break were almost maximum. \n \n \n \nDer Einflus des Styrolgehalts auf die Eigenschaften von elektronenstrahlvernetztem, rusgefulltem Styrol-Butadien-Kautschuk (SBR) war nur bei niedrigen Strahlungsdosen, d. h. geringen Vernetzungsgraden, ausgepragt. Bei hohen Dosen wurde kein Effekt beobachtet, insbesondere fur ZnO-enthaltenden SBR. Es wurde auserdem festgestellt, das ZnO (3 phr) die Zugfestigkeit von SBR mit einem Styrolgehalt von 23,5 Gew.-% bei 20 kGy um 20% verbesserte, verglichen mit SBR mit 46 Gew.-% Styrol. Die Zunahme der Zugfestigkeit fur gefullten SBR (23,5%) betrug bei allen Strahlungsdosen nahezu 17%. Daneben waren Reisfestigkeit, Abrasionswiderstand und Bruchdehnung erheblich verbessert. Die hohe Effizienz von ZnO bei SBR (23,5%) konnte auf dessen hoheren Butadiengehalt zuruckzufuhren sein. Das mechanische Verhalten von SBR (46%) bei 20 kGy war uberraschend, da sowohl Zugfestigkeit als auch Bruchdehnung nahezu maximal waren.","PeriodicalId":7808,"journal":{"name":"Angewandte Makromolekulare Chemie","volume":"87 1","pages":"11-21"},"PeriodicalIF":0.0000,"publicationDate":"1994-05-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"6","resultStr":"{\"title\":\"Effect of styrene content and ZnO-stearic acid on the mechanical properties of radiation-vulcanized styrene-butadiene rubber (SBR)\",\"authors\":\"H. A. Youssef, M. Aziz, F. Yoshii, K. Makuuchi, A. A. Miligy\",\"doi\":\"10.1002/APMC.1994.052180102\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The effect of styrene content on the properties of electron irradiation-vulcanized SBR loaded with carbon black was pronounced only at low irradiation doses where the crosslinking densities were not so high. At high doses, no effect was observed especially for SBR containing ZnO. It was also observed that ZnO (3 phr) increased the tensile strength of SBR containing 23.5 wt.-% styrene by 20% at 20 kGy irradiation dose, compared to 5% at higher doses for SBR containing 46 wt.-% styrene. However, the increase in tensile strength by ZnO for loaded SBR (23.5%) was almost 17% at all irradiation doses. Besides, tear strength, abrasion resistance and elongation at break were remarkably improved. The high efficiency of ZnO toward SBR (23.5%) may be attributed to the higher butadiene content. The behavior of SBR (46%) at 20 kGy was surprising, since both tensile strength and elongation at break were almost maximum. \\n \\n \\n \\nDer Einflus des Styrolgehalts auf die Eigenschaften von elektronenstrahlvernetztem, rusgefulltem Styrol-Butadien-Kautschuk (SBR) war nur bei niedrigen Strahlungsdosen, d. h. geringen Vernetzungsgraden, ausgepragt. Bei hohen Dosen wurde kein Effekt beobachtet, insbesondere fur ZnO-enthaltenden SBR. Es wurde auserdem festgestellt, das ZnO (3 phr) die Zugfestigkeit von SBR mit einem Styrolgehalt von 23,5 Gew.-% bei 20 kGy um 20% verbesserte, verglichen mit SBR mit 46 Gew.-% Styrol. Die Zunahme der Zugfestigkeit fur gefullten SBR (23,5%) betrug bei allen Strahlungsdosen nahezu 17%. Daneben waren Reisfestigkeit, Abrasionswiderstand und Bruchdehnung erheblich verbessert. Die hohe Effizienz von ZnO bei SBR (23,5%) konnte auf dessen hoheren Butadiengehalt zuruckzufuhren sein. Das mechanische Verhalten von SBR (46%) bei 20 kGy war uberraschend, da sowohl Zugfestigkeit als auch Bruchdehnung nahezu maximal waren.\",\"PeriodicalId\":7808,\"journal\":{\"name\":\"Angewandte Makromolekulare Chemie\",\"volume\":\"87 1\",\"pages\":\"11-21\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1994-05-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"6\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Angewandte Makromolekulare Chemie\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1002/APMC.1994.052180102\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Angewandte Makromolekulare Chemie","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1002/APMC.1994.052180102","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 6
摘要
苯乙烯含量对负载炭黑的电子辐照硫化SBR性能的影响仅在低辐照剂量、交联密度不高的情况下才明显。在高剂量下,没有观察到特别对含有ZnO的SBR的影响。在20 kGy的辐照剂量下,ZnO (3 phr)使含23.5 wt.-%苯乙烯的SBR的抗拉强度提高了20%,而含46 wt.-%苯乙烯的SBR的抗拉强度在更高剂量下提高了5%。然而,在所有辐照剂量下,ZnO对负载SBR的拉伸强度增加了23.5%,几乎达到17%。撕裂强度、耐磨性和断裂伸长率均有显著提高。ZnO对SBR的催化效率高达23.5%,这可能归因于其较高的丁二烯含量。SBR(46%)在20 kGy时的表现令人惊讶,因为拉伸强度和断裂伸长率几乎都达到了最大值。[2]刘建军,刘建军,李建军,等。基于电子特征分析的电子特征分析方法研究,电子特征分析方法研究。本文研究了zno -焓变SBR的反应机理。2 .研究了ZnO (3phr)在SBR中的应用,并对其性能进行了分析。-% bei 20 kGy和20% verbesserte, verglichen mit SBR 46 Gew。苯乙烯- %。Die Zunahme der zugfestkeit fur gefullten SBR (23.5%), beallen strahlunsdosen nahesu(17%)。本研究的主要内容有:磨耗性研究、磨耗性研究、磨耗性研究和磨耗性研究。zzzienz von ZnO bei SBR(23,5%)是一种有效的制备氧化锌的方法。Das mechanische Verhalten von SBR (46%) be20 kGy战争中,da sowohl zugfeskekeals等Bruchdehnung nahesu最大预警。
Effect of styrene content and ZnO-stearic acid on the mechanical properties of radiation-vulcanized styrene-butadiene rubber (SBR)
The effect of styrene content on the properties of electron irradiation-vulcanized SBR loaded with carbon black was pronounced only at low irradiation doses where the crosslinking densities were not so high. At high doses, no effect was observed especially for SBR containing ZnO. It was also observed that ZnO (3 phr) increased the tensile strength of SBR containing 23.5 wt.-% styrene by 20% at 20 kGy irradiation dose, compared to 5% at higher doses for SBR containing 46 wt.-% styrene. However, the increase in tensile strength by ZnO for loaded SBR (23.5%) was almost 17% at all irradiation doses. Besides, tear strength, abrasion resistance and elongation at break were remarkably improved. The high efficiency of ZnO toward SBR (23.5%) may be attributed to the higher butadiene content. The behavior of SBR (46%) at 20 kGy was surprising, since both tensile strength and elongation at break were almost maximum.
Der Einflus des Styrolgehalts auf die Eigenschaften von elektronenstrahlvernetztem, rusgefulltem Styrol-Butadien-Kautschuk (SBR) war nur bei niedrigen Strahlungsdosen, d. h. geringen Vernetzungsgraden, ausgepragt. Bei hohen Dosen wurde kein Effekt beobachtet, insbesondere fur ZnO-enthaltenden SBR. Es wurde auserdem festgestellt, das ZnO (3 phr) die Zugfestigkeit von SBR mit einem Styrolgehalt von 23,5 Gew.-% bei 20 kGy um 20% verbesserte, verglichen mit SBR mit 46 Gew.-% Styrol. Die Zunahme der Zugfestigkeit fur gefullten SBR (23,5%) betrug bei allen Strahlungsdosen nahezu 17%. Daneben waren Reisfestigkeit, Abrasionswiderstand und Bruchdehnung erheblich verbessert. Die hohe Effizienz von ZnO bei SBR (23,5%) konnte auf dessen hoheren Butadiengehalt zuruckzufuhren sein. Das mechanische Verhalten von SBR (46%) bei 20 kGy war uberraschend, da sowohl Zugfestigkeit als auch Bruchdehnung nahezu maximal waren.