氯化铬对聚丙烯表面改性的研究

I. Novák, V. Pollák
{"title":"氯化铬对聚丙烯表面改性的研究","authors":"I. Novák, V. Pollák","doi":"10.1002/APMC.1994.052200116","DOIUrl":null,"url":null,"abstract":"The changes of the adhesion properties of isotactic polypropylene (iPP) modified by chromylchloride (CrCl) have been studied. The free surface energy (FSE) of the iPP increases with the time of the modification and reaches a constant value after the time which strongly depends on the temperature of the modification. A similar trend has been observed for the dependences of the FSE vs. concentration of carbonyl groups. The molecular weight of the modified iPP decreases with the temperature of modification. The decrease of the FSE with time is negligible. It was found that after modification of iPP with CrCl the increase of mechanical work of adhesion was higher by 36% than that with chromosulfuric acid. \n \n \n \nDie Anderungen der Adhasionseigenschaften von mit Chromylchlorid modifiziertem isotaktischem Polypropylen (iPP) wurden untersucht. Die freie Oberflachenenergie (FSE) des isotaktischen Polypropylens nimmt mit der Reaktionszeit zu und hangt stark von der Modifikationstemperatur ab. Gleiches gilt fur die Abhangigkeit der FSE von der Konzentration der Carbonylgruppen. Das Molekulargewicht des modifizierten iPP sinkt mit steigender Temperatur der Modifikation. Die Abnahme der FSE mit der Zeit ist gering. Nach der Modifizierung des iPP mit CrCl war der Zuwachs der mechanischen Adhasionsarbeit um 36% hoher als nach der Modifikation mit Chromschwefelsaure.","PeriodicalId":7808,"journal":{"name":"Angewandte Makromolekulare Chemie","volume":"48 1","pages":"189-197"},"PeriodicalIF":0.0000,"publicationDate":"1994-03-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"12","resultStr":"{\"title\":\"Surface modification of polypropylene by chromylchloride\",\"authors\":\"I. Novák, V. Pollák\",\"doi\":\"10.1002/APMC.1994.052200116\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The changes of the adhesion properties of isotactic polypropylene (iPP) modified by chromylchloride (CrCl) have been studied. The free surface energy (FSE) of the iPP increases with the time of the modification and reaches a constant value after the time which strongly depends on the temperature of the modification. A similar trend has been observed for the dependences of the FSE vs. concentration of carbonyl groups. The molecular weight of the modified iPP decreases with the temperature of modification. The decrease of the FSE with time is negligible. It was found that after modification of iPP with CrCl the increase of mechanical work of adhesion was higher by 36% than that with chromosulfuric acid. \\n \\n \\n \\nDie Anderungen der Adhasionseigenschaften von mit Chromylchlorid modifiziertem isotaktischem Polypropylen (iPP) wurden untersucht. Die freie Oberflachenenergie (FSE) des isotaktischen Polypropylens nimmt mit der Reaktionszeit zu und hangt stark von der Modifikationstemperatur ab. Gleiches gilt fur die Abhangigkeit der FSE von der Konzentration der Carbonylgruppen. Das Molekulargewicht des modifizierten iPP sinkt mit steigender Temperatur der Modifikation. Die Abnahme der FSE mit der Zeit ist gering. Nach der Modifizierung des iPP mit CrCl war der Zuwachs der mechanischen Adhasionsarbeit um 36% hoher als nach der Modifikation mit Chromschwefelsaure.\",\"PeriodicalId\":7808,\"journal\":{\"name\":\"Angewandte Makromolekulare Chemie\",\"volume\":\"48 1\",\"pages\":\"189-197\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1994-03-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"12\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Angewandte Makromolekulare Chemie\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1002/APMC.1994.052200116\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Angewandte Makromolekulare Chemie","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1002/APMC.1994.052200116","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 12

摘要

研究了氯化铬(CrCl)改性等规聚丙烯(iPP)黏附性能的变化。iPP的自由表面能(FSE)随改性时间的延长而增大,并在改性后达到一个恒定值,该值与改性温度密切相关。类似的趋势已被观察到的依赖的FSE与羰基的浓度。改性后的iPP分子量随改性温度的升高而降低。FSE随时间的减小可以忽略不计。结果表明,用氯化铬改性iPP后,其粘接机械功的增加量比用硫酸改性iPP的增加量高36%。聚丙烯(iPP)粘接特性的研究。聚丙基改性实验室的实验结果表明,聚丙基改性实验室的实验结果表明,聚丙基改性实验室的实验结果表明,聚丙基改性实验室的实验结果表明,聚丙基改性实验室的实验结果表明,聚丙基改性实验室的实验结果表明,聚丙基改性实验室的实验结果表明,聚丙基改性实验室的实验结果表明,聚丙基改性实验室的实验结果表明:本文研究了一种分子大分子量改性iPP熔池的高温改性方法。Die Abnahme der FSE mit der Zeit ist ering。nder Modifizierung - iPP、CrCl和Zuwachs的粘接机理分别为36%和36%,nder modififierung - chromschweure。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Surface modification of polypropylene by chromylchloride
The changes of the adhesion properties of isotactic polypropylene (iPP) modified by chromylchloride (CrCl) have been studied. The free surface energy (FSE) of the iPP increases with the time of the modification and reaches a constant value after the time which strongly depends on the temperature of the modification. A similar trend has been observed for the dependences of the FSE vs. concentration of carbonyl groups. The molecular weight of the modified iPP decreases with the temperature of modification. The decrease of the FSE with time is negligible. It was found that after modification of iPP with CrCl the increase of mechanical work of adhesion was higher by 36% than that with chromosulfuric acid. Die Anderungen der Adhasionseigenschaften von mit Chromylchlorid modifiziertem isotaktischem Polypropylen (iPP) wurden untersucht. Die freie Oberflachenenergie (FSE) des isotaktischen Polypropylens nimmt mit der Reaktionszeit zu und hangt stark von der Modifikationstemperatur ab. Gleiches gilt fur die Abhangigkeit der FSE von der Konzentration der Carbonylgruppen. Das Molekulargewicht des modifizierten iPP sinkt mit steigender Temperatur der Modifikation. Die Abnahme der FSE mit der Zeit ist gering. Nach der Modifizierung des iPP mit CrCl war der Zuwachs der mechanischen Adhasionsarbeit um 36% hoher als nach der Modifikation mit Chromschwefelsaure.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
自引率
0.00%
发文量
0
期刊最新文献
Copolymerization of styrene with butadiene using methyl tert‐butyl ether as active center modifier Comparison of poly(2,5-dibutoxy-p-phenylenevinylene)s synthesized by two different methods Electro‐optic birefringence and scattering of concentrated solutions of ethylcellulose Photovieillissement d'un copolymère d'éthylène et d'acétate de vinyle en présence de sueur artificielle. II. Evolution morphologique N‐Oxyl‐kontrollierte radikalische Lösungspolymerisation von Styrol
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1