Metal ion binding properties of synthetic vinyl resins

The synthesis of a water-insoluble chelating resin was carried out by radical copolymerization of 4-vinylpyridine and N-hydroxymethyl acrylamide with subsequent crosslinking. Both the crosslinked reference homopolymers of 4-vinylpyridine and N-hydroxymethyl acrylamide were also synthesized. The resins were characterized by elemental analyses and FT-IR spectroscopy. The ability of these resins to bind copper(II), iron(II), iron(III) and uranyl ions as well as the elution of the metal ions from the loaded resins were studied. For uranyl ions, pH 1 was the optimum sorption pH value for all the resins. Sorption selectivity from the binary mixture Cu(II) + U(VI) was studied at the optimum sorption pH value. Finally, the uranium(VI) sorption isotherms, binding constants, and ΔG°, ΔH° and ΔS° corresponding to the uranium(VI) sorption process were calculated. Ein wasserunlosliches chelatisierendes Polymerharz wurde durch radikalische Copolymerisation von 4-Vinylpyridin und N-Hydroxymethylacrylamid und anschliesende Vernetzung hergestellt. Die beiden ebenfalls vernetzten Homopolymeren von 4-Vinylpyridin bzw. N-Hydroxymethylacrylamid wurden ebenfalls synthetisiert. Die Polymeren wurden mittels Elementaranalyse und FT-IR Spektroskopie charakterisiert. Die Adsorptionseigenschaften dieser Harze fur Cu(II)-, Fe(II)-, Fe(III)- und U(VI)-Ionen und die Elution dieser Metallionen von den beladenen Harzen wurde untersucht. Der optimale pH-Wert fur die Aufnahme von Uranylionen liegt bei 1. Bei diesem pH-Wert wurde die Selektivitat der Harze fur die Aufnahme der Ionen aus der binaren Mischung Cu(II)/U(VI) untersucht. Fur die Sorption von Uranylionen wurden die Adsorptionsisothermen, die Bindungskonstanten sowie ΔG°-, ΔH°- und ΔS°-Werte bestimmt.