Y. S. Soebianto, F. Yoshii, K. Makuuchi, I. Ishigaki
{"title":"亲水单体在聚(4‐甲基戊烯‐1)上的辐射接枝,II。长链单体的接枝及接枝膜的物理性质","authors":"Y. S. Soebianto, F. Yoshii, K. Makuuchi, I. Ishigaki","doi":"10.1002/APMC.1987.051520114","DOIUrl":null,"url":null,"abstract":"Radiation grafting of 2-hydroxyethyl methacrylate (HEMA) and methoxytetraethyleneglycol methacrylate (M4G) on low crystallinity poly(4-methylpentene-1) (TPX) has been investigated. Grafting yield increased with increasing pre-irradiation dose, grafting temperature, and monomer concentration. Grafting rate depends on length of molecular chain in the monomers and decreases with increasing chain length. The grafting yields of electron beam irradiated samples were higher than those of γ-irradiated ones because of higher radical concentration. Tensile strength of the grafted film in the dried state increased and the elongation at break decreased with increasing degree of grafting. On the other hand, in the wet state, the tensile strength and elongation at break decreased with increasing the degree of grafting due to the lack of hydrogen bonds between the grafted chains caused by increased water absorption. \n \n \n \nDie strahleninduzierte Pfropfung von 2-Hydroxyethylmethacrylat (HEMA) und Methoxytetraethylenglycolmethacrylat (M4G) auf Poly(4-methylpenten-1) (TPX) wurde untersucht. Die Pfropfungsgrade erhohten sich mit zunehmender Vorbestrahlungsdosis, Pfropfungstemperatur und Monomerkonzentration. Die Pfropfungsgeschwindigkeit ist abhangig von der Kettenlange der Monomeren; sie nimmt mit wachsender Kettenlange ab. Bei Bestrahlen der Filme mit Elektronenstrahlen anstelle von γ-Strahlen waren die Pfropfungsgrade hoher. Die Zugfestigkeit der gepfropften Filme im trockenen Zustand stieg mit zunehmendem Pfropfungsgrad an, wahrend die Bruchdehnung abnahm. Dagegen nahmen die Zugfestigkeit und die Bruchdehnung im nassen Zustand mit wachsendem Pfropfungsgrad ab, da Wasserstoffbruckenbindungen zwischen den aufgepfropften Ketten durch die Wasseraufnahme der Filme fehlten.","PeriodicalId":7808,"journal":{"name":"Angewandte Makromolekulare Chemie","volume":"2 1","pages":"159-168"},"PeriodicalIF":0.0000,"publicationDate":"1987-07-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"7","resultStr":"{\"title\":\"Radiation grafting of hydrophilic monomers onto poly(4‐methylpentene‐1), II. Grafting of long chain monomers and physical properties of the grafted films\",\"authors\":\"Y. S. Soebianto, F. Yoshii, K. Makuuchi, I. Ishigaki\",\"doi\":\"10.1002/APMC.1987.051520114\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Radiation grafting of 2-hydroxyethyl methacrylate (HEMA) and methoxytetraethyleneglycol methacrylate (M4G) on low crystallinity poly(4-methylpentene-1) (TPX) has been investigated. Grafting yield increased with increasing pre-irradiation dose, grafting temperature, and monomer concentration. Grafting rate depends on length of molecular chain in the monomers and decreases with increasing chain length. The grafting yields of electron beam irradiated samples were higher than those of γ-irradiated ones because of higher radical concentration. Tensile strength of the grafted film in the dried state increased and the elongation at break decreased with increasing degree of grafting. On the other hand, in the wet state, the tensile strength and elongation at break decreased with increasing the degree of grafting due to the lack of hydrogen bonds between the grafted chains caused by increased water absorption. \\n \\n \\n \\nDie strahleninduzierte Pfropfung von 2-Hydroxyethylmethacrylat (HEMA) und Methoxytetraethylenglycolmethacrylat (M4G) auf Poly(4-methylpenten-1) (TPX) wurde untersucht. Die Pfropfungsgrade erhohten sich mit zunehmender Vorbestrahlungsdosis, Pfropfungstemperatur und Monomerkonzentration. Die Pfropfungsgeschwindigkeit ist abhangig von der Kettenlange der Monomeren; sie nimmt mit wachsender Kettenlange ab. Bei Bestrahlen der Filme mit Elektronenstrahlen anstelle von γ-Strahlen waren die Pfropfungsgrade hoher. Die Zugfestigkeit der gepfropften Filme im trockenen Zustand stieg mit zunehmendem Pfropfungsgrad an, wahrend die Bruchdehnung abnahm. Dagegen nahmen die Zugfestigkeit und die Bruchdehnung im nassen Zustand mit wachsendem Pfropfungsgrad ab, da Wasserstoffbruckenbindungen zwischen den aufgepfropften Ketten durch die Wasseraufnahme der Filme fehlten.\",\"PeriodicalId\":7808,\"journal\":{\"name\":\"Angewandte Makromolekulare Chemie\",\"volume\":\"2 1\",\"pages\":\"159-168\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1987-07-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"7\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Angewandte Makromolekulare Chemie\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1002/APMC.1987.051520114\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Angewandte Makromolekulare Chemie","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1002/APMC.1987.051520114","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 7
摘要
研究了低结晶度聚(4-甲基戊烯-1)(TPX)上2-甲基丙烯酸羟乙酯(HEMA)和甲氧基甲基丙烯酸四乙二醇(M4G)的辐射接枝反应。接枝收率随辐照前剂量、接枝温度和单体浓度的增加而增加。接枝速率取决于单体中分子链的长度,并随链长的增加而降低。由于自由基浓度较高,电子束辐照样品的接枝率高于γ辐照样品。随着接枝程度的增加,接枝膜在干燥状态下的拉伸强度增加,断裂伸长率降低。另一方面,在湿态下,随着接枝程度的增加,接枝链之间的氢键缺失,导致接枝链的抗拉强度和断裂伸长率下降。2-羟乙基甲基丙烯酸酯(HEMA)和甲氧基四乙基乙二醇甲基丙烯酸酯(M4G)或聚(4-甲基戊烯-1)(TPX)的制备方法。原菌类的分级研究,包括对原菌类温度和单体富集的研究。Die pfropfungsgeswindigkeit ist abhangig von der Kettenlange der Monomeren;您nimmt麻省理工学院wachsender Kettenlange ab。贝Bestrahlen der Filme麻省理工学院Elektronenstrahlen anstelle冯γ-Strahlen waren Pfropfungsgrade死啊。在德国,我们的研究对象是德国的研究对象,我们的研究对象是德国的研究对象。Dagegen,死Zugfestigkeit和死Bruchdehnung im nassen Zustand麻省理工学院wachsendem Pfropfungsgrad ab, da Wasserstoffbruckenbindungen说是窝aufgepfropften Ketten军队死Wasseraufnahme der Filme fehlten。
Radiation grafting of hydrophilic monomers onto poly(4‐methylpentene‐1), II. Grafting of long chain monomers and physical properties of the grafted films
Radiation grafting of 2-hydroxyethyl methacrylate (HEMA) and methoxytetraethyleneglycol methacrylate (M4G) on low crystallinity poly(4-methylpentene-1) (TPX) has been investigated. Grafting yield increased with increasing pre-irradiation dose, grafting temperature, and monomer concentration. Grafting rate depends on length of molecular chain in the monomers and decreases with increasing chain length. The grafting yields of electron beam irradiated samples were higher than those of γ-irradiated ones because of higher radical concentration. Tensile strength of the grafted film in the dried state increased and the elongation at break decreased with increasing degree of grafting. On the other hand, in the wet state, the tensile strength and elongation at break decreased with increasing the degree of grafting due to the lack of hydrogen bonds between the grafted chains caused by increased water absorption.
Die strahleninduzierte Pfropfung von 2-Hydroxyethylmethacrylat (HEMA) und Methoxytetraethylenglycolmethacrylat (M4G) auf Poly(4-methylpenten-1) (TPX) wurde untersucht. Die Pfropfungsgrade erhohten sich mit zunehmender Vorbestrahlungsdosis, Pfropfungstemperatur und Monomerkonzentration. Die Pfropfungsgeschwindigkeit ist abhangig von der Kettenlange der Monomeren; sie nimmt mit wachsender Kettenlange ab. Bei Bestrahlen der Filme mit Elektronenstrahlen anstelle von γ-Strahlen waren die Pfropfungsgrade hoher. Die Zugfestigkeit der gepfropften Filme im trockenen Zustand stieg mit zunehmendem Pfropfungsgrad an, wahrend die Bruchdehnung abnahm. Dagegen nahmen die Zugfestigkeit und die Bruchdehnung im nassen Zustand mit wachsendem Pfropfungsgrad ab, da Wasserstoffbruckenbindungen zwischen den aufgepfropften Ketten durch die Wasseraufnahme der Filme fehlten.