{"title":"气相分解氧化铝初期烧结的重排过程","authors":"Shuzo Kato, T. Iga, Hiromi Sarai","doi":"10.2109/JCERSJ1950.83.17","DOIUrl":null,"url":null,"abstract":"An apparent activation energy for the rearrangement process in the initial stage of sintering was determined in the temperature range from 1400° to 1600°C on vapor phase decomposed alumina.The slopes of log-log plots for the shrinkage of this alumina were unity. From this result it was concluded that the rearrangement process occurred in the early stage of sintering. The apparent activation energy for the process was 45kcal/mol. This value was far lower than that obtained for various diffusion processes.","PeriodicalId":17274,"journal":{"name":"Journal of the Ceramic Association, Japan","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"1975-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Rearrangement Process in the Initial Stage Sintering of Vapor Phase Decomposed Alumina\",\"authors\":\"Shuzo Kato, T. Iga, Hiromi Sarai\",\"doi\":\"10.2109/JCERSJ1950.83.17\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"An apparent activation energy for the rearrangement process in the initial stage of sintering was determined in the temperature range from 1400° to 1600°C on vapor phase decomposed alumina.The slopes of log-log plots for the shrinkage of this alumina were unity. From this result it was concluded that the rearrangement process occurred in the early stage of sintering. The apparent activation energy for the process was 45kcal/mol. This value was far lower than that obtained for various diffusion processes.\",\"PeriodicalId\":17274,\"journal\":{\"name\":\"Journal of the Ceramic Association, Japan\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1975-01-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Journal of the Ceramic Association, Japan\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.2109/JCERSJ1950.83.17\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of the Ceramic Association, Japan","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.2109/JCERSJ1950.83.17","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Rearrangement Process in the Initial Stage Sintering of Vapor Phase Decomposed Alumina
An apparent activation energy for the rearrangement process in the initial stage of sintering was determined in the temperature range from 1400° to 1600°C on vapor phase decomposed alumina.The slopes of log-log plots for the shrinkage of this alumina were unity. From this result it was concluded that the rearrangement process occurred in the early stage of sintering. The apparent activation energy for the process was 45kcal/mol. This value was far lower than that obtained for various diffusion processes.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们