Charge storage properties of HfO2/Ge-HfO2/SiO2 trilayer structures

We report on the charge storage properties of trilayer structures consisting in sputtered gate HfO2/co-sputtered Ge-HfO2 layer/rapid thermal tunneling SiO2 oxide. Investigations of transmission electron microscopy and X-ray diffraction evidence the formation of HfO2 with mixed structure of monoclinic and tetragonal in the annealed structures. Capacitance-voltage (C-V) characteristics were measured on Al/HfO2/Ge-HfO2/SiO2/Si/Al metal-oxide-semiconductor capacitors based on as-deposited and annealed structures. Large C-V hysteresis is observed for the as-deposited structures and is controlled by traps present in oxide and interface. The annealing yields a C-V hysteresis with smaller memory window being due to injected charges in Ge nanocrystals.