H. Dubey, L. Deshmukh, D. Kshirsagar, M. Sharon, M. Sharon
{"title":"SbTeI的合成及电性能研究","authors":"H. Dubey, L. Deshmukh, D. Kshirsagar, M. Sharon, M. Sharon","doi":"10.1155/2014/965350","DOIUrl":null,"url":null,"abstract":"Needle shaped SbTeI crystals were obtained by solid state reaction. Electrical resistance was measured in the temperature range of 4 K to 550 K. SbTeI shows a metallic behavior from 4 K to 300 K, and at higher temperature (>300 K), it shows semiconducting behavior. Unlike SbSI, this material shows almost zero resistance around 550 K. It shows a piezoelectric behavior with a capacitance of 717 pF and its carrier density and nobilities are found to be 2.12 × 1016 cm−3 and 1.01 cm2/(V·s), respectively. Crystals of SbTeI are characterized by XRD, SEM, and Raman analysis. Electrical activation energy is found to be 0.52 eV. It is suggested that this material may be studied for its application as a superconductor with Tc higher than room temperature.","PeriodicalId":7371,"journal":{"name":"Advances in Physical Chemistry","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2014-01-09","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"5","resultStr":"{\"title\":\"Synthesis and Study of Electrical Properties of SbTeI\",\"authors\":\"H. Dubey, L. Deshmukh, D. Kshirsagar, M. Sharon, M. Sharon\",\"doi\":\"10.1155/2014/965350\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Needle shaped SbTeI crystals were obtained by solid state reaction. Electrical resistance was measured in the temperature range of 4 K to 550 K. SbTeI shows a metallic behavior from 4 K to 300 K, and at higher temperature (>300 K), it shows semiconducting behavior. Unlike SbSI, this material shows almost zero resistance around 550 K. It shows a piezoelectric behavior with a capacitance of 717 pF and its carrier density and nobilities are found to be 2.12 × 1016 cm−3 and 1.01 cm2/(V·s), respectively. Crystals of SbTeI are characterized by XRD, SEM, and Raman analysis. Electrical activation energy is found to be 0.52 eV. It is suggested that this material may be studied for its application as a superconductor with Tc higher than room temperature.\",\"PeriodicalId\":7371,\"journal\":{\"name\":\"Advances in Physical Chemistry\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2014-01-09\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"5\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Advances in Physical Chemistry\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1155/2014/965350\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Advances in Physical Chemistry","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1155/2014/965350","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Synthesis and Study of Electrical Properties of SbTeI
Needle shaped SbTeI crystals were obtained by solid state reaction. Electrical resistance was measured in the temperature range of 4 K to 550 K. SbTeI shows a metallic behavior from 4 K to 300 K, and at higher temperature (>300 K), it shows semiconducting behavior. Unlike SbSI, this material shows almost zero resistance around 550 K. It shows a piezoelectric behavior with a capacitance of 717 pF and its carrier density and nobilities are found to be 2.12 × 1016 cm−3 and 1.01 cm2/(V·s), respectively. Crystals of SbTeI are characterized by XRD, SEM, and Raman analysis. Electrical activation energy is found to be 0.52 eV. It is suggested that this material may be studied for its application as a superconductor with Tc higher than room temperature.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们