Effects of temperature and load during hot impression behavior of Cr-Ni stainless steel

Austenitic Stainless steels are majorly used because of their high resistance to aqueous corrosion and high temperature properties. Some major applications of stainless steels at high temperatures include engine and exhaust components in aircrafts, recuperators in steel mills, and pulverized coal injection lances for blast furnaces. In all the above said applications, the components are constantly subjected to loads and high temperatures. This makes the study of their creep behavior very important to decide the life of the component. Cr-Ni stainless steel was used as a starting material, and hot impression creep test was performed on cylindrical samples of 10 mm height and 15 mm diameter for a dwell time of 150 min at two different loads of 84 and 98 MPa and at two different temperatures 450 and 500 °C. The time vs. indentation depth was plotted, and creep rate was calculated in each case. It was observed that with an increase in time, creep rate increased in the primary creep region and remained almost constant in the secondary creep region irrespective of temperature and load. The indentation depth and creep rate increased with an increase in load and temperature.