聚二甲基硅氧烷-聚酰胺多嵌段共聚物超薄膜表面性能的研究

A. Kishida, T. Furuzono, T. Ohshige, I. Maruyama, Matsumoto Takeo, Haruhiko Itoh, M. Murakami, M. Akashi
{"title":"聚二甲基硅氧烷-聚酰胺多嵌段共聚物超薄膜表面性能的研究","authors":"A. Kishida, T. Furuzono, T. Ohshige, I. Maruyama, Matsumoto Takeo, Haruhiko Itoh, M. Murakami, M. Akashi","doi":"10.1002/APMC.1994.052200108","DOIUrl":null,"url":null,"abstract":"Ultrathin films of poly(dimethylsiloxane)-polyamide copolymers (PAS) with different silicone contents were prepared by the methods of water casting and spin coating. The surface properties of the films were investigated in detail using contact angle measurements and X-ray photoelectron spectroscopy (XPS). The water-cast films were thin enough to be applicable as laminate films for an artificial lung or an air-separator for oxygen-enrichted air. Uniform and ultrathin films were obtained by the spin coating method. XPS and contact angle measurements suggested that poly(dimethylsiloxane) segments were condensed at the outermost surface of spin-coated PAS films. XPS measurements also revealed that the surface properties of PAS were affected by the molding method, especially the solvent evaporation conditions. \n \n \n \nUltradunne Filme aus Polydimethylsiloxan(PDMS)-Polyamid-Copolymeren (PAS) mit unterschiedlichen Silikonanteilen wurden durch Filmgiesen auf Wasser und Rotationsbeschichten hergestellt. Die Oberflacheneigenschaften der Filme wurden mittels Kontaktwinkelmessungen und Rontgenphotoelektronenspektroskopie (XPS) untersucht. Die auf Wasser gegossenen Filme waren dunn genug, um als Laminatfilme in kunstlichen Lungen oder als Trennmembranen zur Sauerstoffanreicherung von Luft Anwendung finden zu konnen. Gleichmasig dicke und ultradunne Filme wurden durch Rotationsbeschichten erhalten. Aus den XPS- und Kontaktwinkelmessungen kann geschlossen werden, das sich die PDMS-Segmente an der Oberflache der Filme anreichern. Aus den XPS-Messungen geht auserdem hervor, das die Oberflacheneigenschaften von PAS von der Herstellungsmethode, insbesondere von den Bedingungen der Losemittelverdampfung abhangen.","PeriodicalId":7808,"journal":{"name":"Angewandte Makromolekulare Chemie","volume":"54 1","pages":"89-97"},"PeriodicalIF":0.0000,"publicationDate":"1994-03-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"13","resultStr":"{\"title\":\"Study of the surface properties of ultrathin films of poly(dimethylsiloxane)‐polyamide multiblock copolymers\",\"authors\":\"A. Kishida, T. Furuzono, T. Ohshige, I. Maruyama, Matsumoto Takeo, Haruhiko Itoh, M. Murakami, M. Akashi\",\"doi\":\"10.1002/APMC.1994.052200108\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Ultrathin films of poly(dimethylsiloxane)-polyamide copolymers (PAS) with different silicone contents were prepared by the methods of water casting and spin coating. The surface properties of the films were investigated in detail using contact angle measurements and X-ray photoelectron spectroscopy (XPS). The water-cast films were thin enough to be applicable as laminate films for an artificial lung or an air-separator for oxygen-enrichted air. Uniform and ultrathin films were obtained by the spin coating method. XPS and contact angle measurements suggested that poly(dimethylsiloxane) segments were condensed at the outermost surface of spin-coated PAS films. XPS measurements also revealed that the surface properties of PAS were affected by the molding method, especially the solvent evaporation conditions. \\n \\n \\n \\nUltradunne Filme aus Polydimethylsiloxan(PDMS)-Polyamid-Copolymeren (PAS) mit unterschiedlichen Silikonanteilen wurden durch Filmgiesen auf Wasser und Rotationsbeschichten hergestellt. Die Oberflacheneigenschaften der Filme wurden mittels Kontaktwinkelmessungen und Rontgenphotoelektronenspektroskopie (XPS) untersucht. Die auf Wasser gegossenen Filme waren dunn genug, um als Laminatfilme in kunstlichen Lungen oder als Trennmembranen zur Sauerstoffanreicherung von Luft Anwendung finden zu konnen. Gleichmasig dicke und ultradunne Filme wurden durch Rotationsbeschichten erhalten. Aus den XPS- und Kontaktwinkelmessungen kann geschlossen werden, das sich die PDMS-Segmente an der Oberflache der Filme anreichern. Aus den XPS-Messungen geht auserdem hervor, das die Oberflacheneigenschaften von PAS von der Herstellungsmethode, insbesondere von den Bedingungen der Losemittelverdampfung abhangen.\",\"PeriodicalId\":7808,\"journal\":{\"name\":\"Angewandte Makromolekulare Chemie\",\"volume\":\"54 1\",\"pages\":\"89-97\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1994-03-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"13\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Angewandte Makromolekulare Chemie\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1002/APMC.1994.052200108\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Angewandte Makromolekulare Chemie","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1002/APMC.1994.052200108","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 13

摘要

采用水铸法制备了不同硅酮含量的聚二甲基硅氧烷-聚酰胺共聚物(PAS)超薄膜。利用接触角测量和x射线光电子能谱(XPS)对膜的表面特性进行了详细的研究。水铸膜足够薄,可以用作人造肺或富氧空气分离器的层压板膜。采用自旋镀膜法获得了均匀的超薄薄膜。XPS和接触角测量表明,聚二甲基硅氧烷片段在自旋涂覆的PAS膜的最外表面凝聚。XPS测试还表明,成型方法,特别是溶剂蒸发条件对聚碳酸酯表面性能的影响较大。聚二甲基硅氧烷(PDMS)-聚酰胺-共聚物(PAS)超粘膜是一种超粘膜材料。电影技术与光电光谱(XPS)研究进展。在电影中,我们发现了一种新的方法,即在电影中找到一种新的方法,即在电影中找到一种新的方法。超高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速高速。与此同时,我们也在为pdms - segment和oberflacher - Filme - erichern提供技术支持。在XPS-Messungen得到auserdem hervor, das die Oberflacheneigenschaften von PAS von der herstellungsmethod, insbesonere von den Bedingungen der Losemittelverdampfung abhangen。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Study of the surface properties of ultrathin films of poly(dimethylsiloxane)‐polyamide multiblock copolymers
Ultrathin films of poly(dimethylsiloxane)-polyamide copolymers (PAS) with different silicone contents were prepared by the methods of water casting and spin coating. The surface properties of the films were investigated in detail using contact angle measurements and X-ray photoelectron spectroscopy (XPS). The water-cast films were thin enough to be applicable as laminate films for an artificial lung or an air-separator for oxygen-enrichted air. Uniform and ultrathin films were obtained by the spin coating method. XPS and contact angle measurements suggested that poly(dimethylsiloxane) segments were condensed at the outermost surface of spin-coated PAS films. XPS measurements also revealed that the surface properties of PAS were affected by the molding method, especially the solvent evaporation conditions. Ultradunne Filme aus Polydimethylsiloxan(PDMS)-Polyamid-Copolymeren (PAS) mit unterschiedlichen Silikonanteilen wurden durch Filmgiesen auf Wasser und Rotationsbeschichten hergestellt. Die Oberflacheneigenschaften der Filme wurden mittels Kontaktwinkelmessungen und Rontgenphotoelektronenspektroskopie (XPS) untersucht. Die auf Wasser gegossenen Filme waren dunn genug, um als Laminatfilme in kunstlichen Lungen oder als Trennmembranen zur Sauerstoffanreicherung von Luft Anwendung finden zu konnen. Gleichmasig dicke und ultradunne Filme wurden durch Rotationsbeschichten erhalten. Aus den XPS- und Kontaktwinkelmessungen kann geschlossen werden, das sich die PDMS-Segmente an der Oberflache der Filme anreichern. Aus den XPS-Messungen geht auserdem hervor, das die Oberflacheneigenschaften von PAS von der Herstellungsmethode, insbesondere von den Bedingungen der Losemittelverdampfung abhangen.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
自引率
0.00%
发文量
0
期刊最新文献
Copolymerization of styrene with butadiene using methyl tert‐butyl ether as active center modifier Comparison of poly(2,5-dibutoxy-p-phenylenevinylene)s synthesized by two different methods Electro‐optic birefringence and scattering of concentrated solutions of ethylcellulose Photovieillissement d'un copolymère d'éthylène et d'acétate de vinyle en présence de sueur artificielle. II. Evolution morphologique N‐Oxyl‐kontrollierte radikalische Lösungspolymerisation von Styrol
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1