{"title":"碳化二亚胺 (EDC) 对环氧树脂类牙髓封闭剂与牙根牙本质粘接强度寿命的影响：体外研究","authors":"Pedro Henrique Bernardes Caetano, Helena Cristina de Assis, Leonardo Moreira Teodosio, Gunther Ricardo Bertolini, Renato Roperto, Manoel Damião Sousa-Neto, Fabiane Carneiro Lopes-Olhê","doi":"10.3290/j.jad.b4097187","DOIUrl":null,"url":null,"abstract":"<p><strong>Purpose: </strong>EDC (1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride) can increase dentin bonding longevity. This study aimed to evaluate the effect of final irrigation of the root canal with EDC on the bond strength (BS) longevity of an epoxy resin-based root-canal sealer.</p><p><strong>Materials and methods: </strong>Twenty maxillary canines were sectioned and standardized for root length at 17 mm. Roots were instrumented and distributed into 2 groups according to the final irrigation protocol: EDTA 17%+NaOCl 2.5% (C) and EDTA 17%+NaOCl 2.5%+EDC 0.5M (EDC). The canals were dried and filled with AH Plus (Dentsply Sirona). Three slices were obtained per third, and the first slice from each third was used for the immediate push-out test (i) followed by analysis of the failure pattern (n = 10); the second slice from each third was used for the push-out test after 6-month aging (A) followed by analysis of the failure pattern (n = 10); the third slice from each third was used to examine the adhesive interface under confocal laser scanning microscopy (CLSM) (n = 10). Data were analyzed with ANOVA, Fisher's exact and Kruskal-Wallis tests.</p><p><strong>Results: </strong>Higher BSs were found for EDC-A (5.6 ± 1.9) than for EDC-I (3.3 ± 0.7), C-i (2.5 ± 1.0) and C-i (2.6 ± 1.0) (p = 0.0001), while C-A values were in some cases similar to C-i and in others similar to EDC-i. No statistically significant difference was observed between the thirds (p > 0.05), except for EDC-i, which showed lower BS for the cervical (2.79 ± 0.46) compared to the apical third (3.8 ± 0.5), while the middle third in some cases had values similar to those of the apical and in others to the cervical third (3.2 ± 0.7) (p = 0.032). More mixed adhesive failures were found in the cervical third, and more adhesive failures to the sealer occurred in the middle and apical thirds (p = 0.014). A significant difference was observed between treatments in terms of adaptation of the adhesive interface, with a higher percentage of good adaptation using EDC (66.7%) than using C (40%), and a lower percentage of poor adaptation with EDC (10%) compared to C (20%) (p < 0.05).</p><p><strong>Conclusion: </strong>Root canal irrigation with EDC increased the longevity of the adhesive interface of an epoxy resin-based root-canal sealer.</p>","PeriodicalId":55604,"journal":{"name":"Journal of Adhesive Dentistry","volume":"25 1","pages":"117-124"},"PeriodicalIF":2.5000,"publicationDate":"2023-05-16","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Effect of Carbodiimide (EDC) on the Bond Strength Longevity of Epoxy Resin-based Endodontic Sealer to Root Dentin: An In-Vitro Study.\",\"authors\":\"Pedro Henrique Bernardes Caetano, Helena Cristina de Assis, Leonardo Moreira Teodosio, Gunther Ricardo Bertolini, Renato Roperto, Manoel Damião Sousa-Neto, Fabiane Carneiro Lopes-Olhê\",\"doi\":\"10.3290/j.jad.b4097187\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p><strong>Purpose: </strong>EDC (1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride) can increase dentin bonding longevity. This study aimed to evaluate the effect of final irrigation of the root canal with EDC on the bond strength (BS) longevity of an epoxy resin-based root-canal sealer.</p><p><strong>Materials and methods: </strong>Twenty maxillary canines were sectioned and standardized for root length at 17 mm. Roots were instrumented and distributed into 2 groups according to the final irrigation protocol: EDTA 17%+NaOCl 2.5% (C) and EDTA 17%+NaOCl 2.5%+EDC 0.5M (EDC). The canals were dried and filled with AH Plus (Dentsply Sirona). Three slices were obtained per third, and the first slice from each third was used for the immediate push-out test (i) followed by analysis of the failure pattern (n = 10); the second slice from each third was used for the push-out test after 6-month aging (A) followed by analysis of the failure pattern (n = 10); the third slice from each third was used to examine the adhesive interface under confocal laser scanning microscopy (CLSM) (n = 10). Data were analyzed with ANOVA, Fisher's exact and Kruskal-Wallis tests.</p><p><strong>Results: </strong>Higher BSs were found for EDC-A (5.6 ± 1.9) than for EDC-I (3.3 ± 0.7), C-i (2.5 ± 1.0) and C-i (2.6 ± 1.0) (p = 0.0001), while C-A values were in some cases similar to C-i and in others similar to EDC-i. No statistically significant difference was observed between the thirds (p > 0.05), except for EDC-i, which showed lower BS for the cervical (2.79 ± 0.46) compared to the apical third (3.8 ± 0.5), while the middle third in some cases had values similar to those of the apical and in others to the cervical third (3.2 ± 0.7) (p = 0.032). More mixed adhesive failures were found in the cervical third, and more adhesive failures to the sealer occurred in the middle and apical thirds (p = 0.014). A significant difference was observed between treatments in terms of adaptation of the adhesive interface, with a higher percentage of good adaptation using EDC (66.7%) than using C (40%), and a lower percentage of poor adaptation with EDC (10%) compared to C (20%) (p < 0.05).</p><p><strong>Conclusion: </strong>Root canal irrigation with EDC increased the longevity of the adhesive interface of an epoxy resin-based root-canal sealer.</p>\",\"PeriodicalId\":55604,\"journal\":{\"name\":\"Journal of Adhesive Dentistry\",\"volume\":\"25 1\",\"pages\":\"117-124\"},\"PeriodicalIF\":2.5000,\"publicationDate\":\"2023-05-16\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Journal of Adhesive Dentistry\",\"FirstCategoryId\":\"3\",\"ListUrlMain\":\"https://doi.org/10.3290/j.jad.b4097187\",\"RegionNum\":3,\"RegionCategory\":\"医学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"DENTISTRY, ORAL SURGERY & MEDICINE\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Adhesive Dentistry","FirstCategoryId":"3","ListUrlMain":"https://doi.org/10.3290/j.jad.b4097187","RegionNum":3,"RegionCategory":"医学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"DENTISTRY, ORAL SURGERY & MEDICINE","Score":null,"Total":0}
Effect of Carbodiimide (EDC) on the Bond Strength Longevity of Epoxy Resin-based Endodontic Sealer to Root Dentin: An In-Vitro Study.
Purpose: EDC (1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride) can increase dentin bonding longevity. This study aimed to evaluate the effect of final irrigation of the root canal with EDC on the bond strength (BS) longevity of an epoxy resin-based root-canal sealer.
Materials and methods: Twenty maxillary canines were sectioned and standardized for root length at 17 mm. Roots were instrumented and distributed into 2 groups according to the final irrigation protocol: EDTA 17%+NaOCl 2.5% (C) and EDTA 17%+NaOCl 2.5%+EDC 0.5M (EDC). The canals were dried and filled with AH Plus (Dentsply Sirona). Three slices were obtained per third, and the first slice from each third was used for the immediate push-out test (i) followed by analysis of the failure pattern (n = 10); the second slice from each third was used for the push-out test after 6-month aging (A) followed by analysis of the failure pattern (n = 10); the third slice from each third was used to examine the adhesive interface under confocal laser scanning microscopy (CLSM) (n = 10). Data were analyzed with ANOVA, Fisher's exact and Kruskal-Wallis tests.
Results: Higher BSs were found for EDC-A (5.6 ± 1.9) than for EDC-I (3.3 ± 0.7), C-i (2.5 ± 1.0) and C-i (2.6 ± 1.0) (p = 0.0001), while C-A values were in some cases similar to C-i and in others similar to EDC-i. No statistically significant difference was observed between the thirds (p > 0.05), except for EDC-i, which showed lower BS for the cervical (2.79 ± 0.46) compared to the apical third (3.8 ± 0.5), while the middle third in some cases had values similar to those of the apical and in others to the cervical third (3.2 ± 0.7) (p = 0.032). More mixed adhesive failures were found in the cervical third, and more adhesive failures to the sealer occurred in the middle and apical thirds (p = 0.014). A significant difference was observed between treatments in terms of adaptation of the adhesive interface, with a higher percentage of good adaptation using EDC (66.7%) than using C (40%), and a lower percentage of poor adaptation with EDC (10%) compared to C (20%) (p < 0.05).
Conclusion: Root canal irrigation with EDC increased the longevity of the adhesive interface of an epoxy resin-based root-canal sealer.
期刊介绍：
New materials and applications for adhesion are profoundly changing the way dentistry is delivered. Bonding techniques, which have long been restricted to the tooth hard tissues, enamel, and dentin, have obvious applications in operative and preventive dentistry, as well as in esthetic and pediatric dentistry, prosthodontics, and orthodontics. The current development of adhesive techniques for soft tissues and slow-releasing agents will expand applications to include periodontics and oral surgery. Scientifically sound, peer-reviewed articles explore the latest innovations in these emerging fields.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们