M. Chirita, R. Banica, P. Sfirloaga, A. Ieta, I. Grozescu
{"title":"A short route of micrometric magnetite synthesis via Fe-EDTA thermal decomposition","authors":"M. Chirita, R. Banica, P. Sfirloaga, A. Ieta, I. Grozescu","doi":"10.1109/SMICND.2010.5650629","DOIUrl":null,"url":null,"abstract":"We develop an procedure for synthesizing micrometric magnetite crystals after two hours of autoclavation at 250°C by hydrothermal decomposition of Fe- Ethylenediaminetetraacetic acid (Fe-EDTA) complex in the presence of urea starting from Fe (III)-Ferric Ammonium Sulfate (FAS), and Na4EDTA as main precursors. Crystals with 10–15 µm in size (along the <001> axis), were obtained. X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy and magnetic measurements were performed to investigate the final product. A low remanent magnetization (5 emu/g) was observed at high level magnetic field intensity (3.8 kOe), emulating superparamagnetic behavior, uncommon for magnetic microparticles at room temperature.","PeriodicalId":377326,"journal":{"name":"CAS 2010 Proceedings (International Semiconductor Conference)","volume":"1 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2010-12-03","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"6","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"CAS 2010 Proceedings (International Semiconductor Conference)","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1109/SMICND.2010.5650629","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 6
Abstract
We develop an procedure for synthesizing micrometric magnetite crystals after two hours of autoclavation at 250°C by hydrothermal decomposition of Fe- Ethylenediaminetetraacetic acid (Fe-EDTA) complex in the presence of urea starting from Fe (III)-Ferric Ammonium Sulfate (FAS), and Na4EDTA as main precursors. Crystals with 10–15 µm in size (along the <001> axis), were obtained. X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy and magnetic measurements were performed to investigate the final product. A low remanent magnetization (5 emu/g) was observed at high level magnetic field intensity (3.8 kOe), emulating superparamagnetic behavior, uncommon for magnetic microparticles at room temperature.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们