C. Hsiao, Chun-Xiao Liu, S. Huynh, T. Minh, H. Yu, Hong-Quan Nguyen, J. Maa, S. Chang, E. Chang
{"title":"Effect of V/III ratios on surface morphology in a GaSb thin film grown on GaAs substrate by MOCVD","authors":"C. Hsiao, Chun-Xiao Liu, S. Huynh, T. Minh, H. Yu, Hong-Quan Nguyen, J. Maa, S. Chang, E. Chang","doi":"10.1109/SMELEC.2014.6920896","DOIUrl":null,"url":null,"abstract":"The epitaxial growth of GaSb thin film with different V/III ratios on high-lattice-mismatched GaAs (001) substrates by metal organic chemical vapor deposition (MOCVD) was investigated. Under optimal V/III ratio of 2.5, we found that there are many periodic 90° interfacial misfit dislocation (IMF) arrays existing at the GaAs/GaSb interface. The surface roughness is about 3.6nm, 2.2nm, 3.8nm, respectively while different V/III ratios (1.25, 2.5, 5) were adopted. These results demonstrated that the hill-and valley structure on the surface of GaSb/GaAs heterostructure can be effectively improved, and formed smooth surface morphology.","PeriodicalId":268203,"journal":{"name":"2014 IEEE International Conference on Semiconductor Electronics (ICSE2014)","volume":"16 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2014-10-13","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"2014 IEEE International Conference on Semiconductor Electronics (ICSE2014)","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1109/SMELEC.2014.6920896","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
The epitaxial growth of GaSb thin film with different V/III ratios on high-lattice-mismatched GaAs (001) substrates by metal organic chemical vapor deposition (MOCVD) was investigated. Under optimal V/III ratio of 2.5, we found that there are many periodic 90° interfacial misfit dislocation (IMF) arrays existing at the GaAs/GaSb interface. The surface roughness is about 3.6nm, 2.2nm, 3.8nm, respectively while different V/III ratios (1.25, 2.5, 5) were adopted. These results demonstrated that the hill-and valley structure on the surface of GaSb/GaAs heterostructure can be effectively improved, and formed smooth surface morphology.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们