Justus Uchenna Anaele, Kenneth Kanayo Alaneme, Joseph Ajibade Omotoyinbo
{"title":"Wear and corrosion behavior of selected up-quenched and step-quenched CuZnSn shape memory alloys","authors":"Justus Uchenna Anaele, Kenneth Kanayo Alaneme, Joseph Ajibade Omotoyinbo","doi":"10.1051/mfreview/2023015","DOIUrl":null,"url":null,"abstract":"The effect of thermal treatment on the wear and corrosion behavior of three categories of Cu-Zn-Sn-Fe SMAs designated A, B, and C is studied. Wear properties were investigated using a tribometer whilst corrosion in 0.3 M H 2 SO 4 and 3.5%NaCl media was studied using the potentiodynamic polarization method. The microstructure of the alloys mainly consists of FCC Cu-rich phase and Cu 5 Zn 8 phase. The up-quenched A alloys show the highest hardness and lowest wear rate values of 72.1 HRB and 0.143 mm 3 /N/m respectively. Average COF was higher for the samples subjected to direct-quenching (0.35–0.12) than the up-quenched (0.16–0.12) and step-quenched (0.2–0.08) samples. Wear occurred by mixed mode mechanisms of abrasion and adhesion evident by grooves and wear particles on the surface. In 0.3 M H 2 SO 4 medium, step-quenched alloys had corrosion rates in the range of 0.1022 to 1.1705 mm/yr, which is lower than the range of 0.1466 to 0.2855 mm/yr, and 0.1730 to 0.6027 mm/yr obtained for direct quenched and up-quenched samples respectively. In 3.5% NaCl solution, step-quenched alloys had the lowest corrosion rates 0.0251 mm/yr relative to samples subjected to up-quenching and direct quenching treatment. Generally, step-quenching treatment effectively improved the corrosion resistance of alloys in both media.","PeriodicalId":51873,"journal":{"name":"Manufacturing Review","volume":"1 1","pages":"0"},"PeriodicalIF":1.9000,"publicationDate":"2023-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Manufacturing Review","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1051/mfreview/2023015","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"ENGINEERING, MANUFACTURING","Score":null,"Total":0}
引用次数: 0
Abstract
The effect of thermal treatment on the wear and corrosion behavior of three categories of Cu-Zn-Sn-Fe SMAs designated A, B, and C is studied. Wear properties were investigated using a tribometer whilst corrosion in 0.3 M H 2 SO 4 and 3.5%NaCl media was studied using the potentiodynamic polarization method. The microstructure of the alloys mainly consists of FCC Cu-rich phase and Cu 5 Zn 8 phase. The up-quenched A alloys show the highest hardness and lowest wear rate values of 72.1 HRB and 0.143 mm 3 /N/m respectively. Average COF was higher for the samples subjected to direct-quenching (0.35–0.12) than the up-quenched (0.16–0.12) and step-quenched (0.2–0.08) samples. Wear occurred by mixed mode mechanisms of abrasion and adhesion evident by grooves and wear particles on the surface. In 0.3 M H 2 SO 4 medium, step-quenched alloys had corrosion rates in the range of 0.1022 to 1.1705 mm/yr, which is lower than the range of 0.1466 to 0.2855 mm/yr, and 0.1730 to 0.6027 mm/yr obtained for direct quenched and up-quenched samples respectively. In 3.5% NaCl solution, step-quenched alloys had the lowest corrosion rates 0.0251 mm/yr relative to samples subjected to up-quenching and direct quenching treatment. Generally, step-quenching treatment effectively improved the corrosion resistance of alloys in both media.
期刊介绍：
The aim of the journal is to stimulate and record an international forum for disseminating knowledge on the advances, developments and applications of manufacturing engineering, technology and applied sciences with a focus on critical reviews of developments in manufacturing and emerging trends in this field. The journal intends to establish a specific focus on reviews of developments of key core topics and on the emerging technologies concerning manufacturing engineering, technology and applied sciences, the aim of which is to provide readers with rapid and easy access to definitive and authoritative knowledge and research-backed opinions on future developments. The scope includes, but is not limited to critical reviews and outstanding original research papers on the advances, developments and applications of: Materials for advanced manufacturing (Metals, Polymers, Glass, Ceramics, Composites, Nano-materials, etc.) and recycling, Material processing methods and technology (Machining, Forming/Shaping, Casting, Powder Metallurgy, Laser technology, Joining, etc.), Additive/rapid manufacturing methods and technology, Tooling and surface-engineering technology (fabrication, coating, heat treatment, etc.), Micro-manufacturing methods and technology, Nano-manufacturing methods and technology, Advanced metrology, instrumentation, quality assurance, testing and inspection, Mechatronics for manufacturing automation, Manufacturing machinery and manufacturing systems, Process chain integration and manufacturing platforms, Sustainable manufacturing and Life-cycle analysis, Industry case studies involving applications of the state-of-the-art manufacturing methods, technology and systems. Content will include invited reviews, original research articles, and invited special topic contributions.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们