Ahmad Abdulhasan Zarkooshi, Murat Kaleli, Nina Tuncel, Iskender Akkurt
{"title":"Physical and chemical properties of beads glasses","authors":"Ahmad Abdulhasan Zarkooshi, Murat Kaleli, Nina Tuncel, Iskender Akkurt","doi":"10.1515/mt-2023-0114","DOIUrl":null,"url":null,"abstract":"Abstract The chemical and physical characterization of glass beads in different sizes with diameters 3 mm, 4 mm, 5 mm and 6 mm, respectively, have been studied in this paper. The X-ray Diffraction (XRD) analysis exhibited that the structure of glass bead is amorphous, and the diffraction peaks for annealing sample 400 °C and 600 °C, respectively, are seen at 2 θ values ranged (26.165°–29.47°). The Scanning Electron Microscopy (SEM) and chemical composition measurement by Energy Dispersive Spectrometer (EDS) system have been conducted; they exhibited that all the samples have the same smooth surface, and the chemical composition analysis showed that the weight percentage of oxygen and silicon were dominant elements in the main structure of glass beads as well as some other elements like Ca, Mg, and Na were observed.","PeriodicalId":18231,"journal":{"name":"Materials Testing","volume":"39 1","pages":"0"},"PeriodicalIF":3.5000,"publicationDate":"2023-09-12","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Testing","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1515/mt-2023-0114","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"MATERIALS SCIENCE, CHARACTERIZATION & TESTING","Score":null,"Total":0}
引用次数: 0
Abstract
Abstract The chemical and physical characterization of glass beads in different sizes with diameters 3 mm, 4 mm, 5 mm and 6 mm, respectively, have been studied in this paper. The X-ray Diffraction (XRD) analysis exhibited that the structure of glass bead is amorphous, and the diffraction peaks for annealing sample 400 °C and 600 °C, respectively, are seen at 2 θ values ranged (26.165°–29.47°). The Scanning Electron Microscopy (SEM) and chemical composition measurement by Energy Dispersive Spectrometer (EDS) system have been conducted; they exhibited that all the samples have the same smooth surface, and the chemical composition analysis showed that the weight percentage of oxygen and silicon were dominant elements in the main structure of glass beads as well as some other elements like Ca, Mg, and Na were observed.
期刊介绍：
Materials Testing is a SCI-listed English language journal dealing with all aspects of material and component testing with a special focus on transfer between laboratory research into industrial application. The journal provides first-hand information on non-destructive, destructive, optical, physical and chemical test procedures. It contains exclusive articles which are peer-reviewed applying respectively high international quality criterions.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们