Nasya K. Mahandini, Donna Hermawati, Oedijani Santoso, Nadia Hardini
{"title":"Pengaruh Variasi pH Saliva terhadap Kekerasan Resin Komposit Bulk-Fill","authors":"Nasya K. Mahandini, Donna Hermawati, Oedijani Santoso, Nadia Hardini","doi":"10.35790/eg.v12i1.48510","DOIUrl":null,"url":null,"abstract":"Abstract: Composite resin is the most widely used restorative material in dentistry. The filling that has been applied will always be in contact with saliva in the oral cavity. This study aimed to determine the effect of salivary pH variations on the hardness of bulk-fill composite resin. This was an experimental study with a post-test only with a control group design. Samples consisted of 28 bulk-fill composite resin samples with 8 mm diameter and 4 mm thickness. Samples were divided into four groups, as follows: group I, soaked in saliva with a pH of 5.3; group II, soaked in saliva with a pH of 6.6; group III, soaked in saliva with a pH of 7.8; and a control group, not treated. The hardness of the samples was measured using Vickers hardness tester. Data were analyzed using the Analysis of Variance (ANOVA) test. The results showed that the mean and standard deviation (SD) hardness values of the bulk-fill composite resin in the control group, groups I, II and II were 63.933 ±4.721 VHN, 63.233±3.518 VHN, 64.683±7.600 VHN, and 69.267±12.545 VHN respectively. These results indicated that there was a decrease in hardness in group I and an increase in hardness in groups II and III. The ANOVA test showed that there was no significant difference in all groups with a p-value of 0.474 (p>0.05). In conclusion, variations in salivary pH do not significantly affect the hardness of bulk-fill composite resin. Keywords: salivary pH; bulk-fill composite resin; hardness of resin Abstrak: Resin komposit merupakan bahan restorasi dibidang kedokteran gigi yang paling banyak digunakan. Tumpatan yang telah diaplikasikan akan selalu berkontak dengan saliva yang terdapat di rongga mulut. Tujuan penelitian ini ialah untuk mengetahui pengaruh variasi pH saliva terhadap kekerasan resin komposit bulk-fill. Jenis penelitian ialah eksperimental dengan post-test only with control group design. Sampel penelitian terdiri dari 28 sampel resin komposit bulk-fill dengan diameter 8 mm dan tinggi 4 mm, yang dibagi menjadi empat kelompok, yaitu: kelompok I direndam pada saliva dengan pH 5,3; kelompok II direndam pada saliva dengan pH 6,6; kelompok III direndam pada saliva dengan pH 7,8; dan kelompok kontrol tidak dilakukan perendaman. Kekerasan sampel diukur menggunakan Vickers hardness tester. Data dianalisis menggunakan uji Analysis of Variance (ANOVA). Hasil penelitian mendapatkan nilai rerata dan standar deviasi (SD) kekerasan resin komposit bulk-fill pada kelompok kontrol, kelompok I, II dan II ialah 63,933±4,721 VHN, 63,233±3,518 VHN, 64,683±7,600 VHN, dan 69,267±12,545 VHN secara berurut. Hasil tersebut menunjukkan bahwa terjadi penurunan kekerasan pada kelompok I dan terjadi peningkatan kekerasan pada kelompok II dan III. Uji ANOVA menunjukkan bahwa tidak terdapat perbedaan bermakna pada semua kelompok dengan nilai p 0,474 (p>0,05). Simpulan penelitian ini ialah variasi pH saliva tidak berpengaruh secara bermakna terhadap kekerasan resin komposit bulk-fill. Kata kunci: pH saliva; resin komposit bulk-fill; kekerasan resin","PeriodicalId":11034,"journal":{"name":"Dental Journal (Majalah Kedokteran Gigi)","volume":"36 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2023-10-10","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Dental Journal (Majalah Kedokteran Gigi)","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.35790/eg.v12i1.48510","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"Dentistry","Score":null,"Total":0}
引用次数: 0
Abstract
Abstract: Composite resin is the most widely used restorative material in dentistry. The filling that has been applied will always be in contact with saliva in the oral cavity. This study aimed to determine the effect of salivary pH variations on the hardness of bulk-fill composite resin. This was an experimental study with a post-test only with a control group design. Samples consisted of 28 bulk-fill composite resin samples with 8 mm diameter and 4 mm thickness. Samples were divided into four groups, as follows: group I, soaked in saliva with a pH of 5.3; group II, soaked in saliva with a pH of 6.6; group III, soaked in saliva with a pH of 7.8; and a control group, not treated. The hardness of the samples was measured using Vickers hardness tester. Data were analyzed using the Analysis of Variance (ANOVA) test. The results showed that the mean and standard deviation (SD) hardness values of the bulk-fill composite resin in the control group, groups I, II and II were 63.933 ±4.721 VHN, 63.233±3.518 VHN, 64.683±7.600 VHN, and 69.267±12.545 VHN respectively. These results indicated that there was a decrease in hardness in group I and an increase in hardness in groups II and III. The ANOVA test showed that there was no significant difference in all groups with a p-value of 0.474 (p>0.05). In conclusion, variations in salivary pH do not significantly affect the hardness of bulk-fill composite resin. Keywords: salivary pH; bulk-fill composite resin; hardness of resin Abstrak: Resin komposit merupakan bahan restorasi dibidang kedokteran gigi yang paling banyak digunakan. Tumpatan yang telah diaplikasikan akan selalu berkontak dengan saliva yang terdapat di rongga mulut. Tujuan penelitian ini ialah untuk mengetahui pengaruh variasi pH saliva terhadap kekerasan resin komposit bulk-fill. Jenis penelitian ialah eksperimental dengan post-test only with control group design. Sampel penelitian terdiri dari 28 sampel resin komposit bulk-fill dengan diameter 8 mm dan tinggi 4 mm, yang dibagi menjadi empat kelompok, yaitu: kelompok I direndam pada saliva dengan pH 5,3; kelompok II direndam pada saliva dengan pH 6,6; kelompok III direndam pada saliva dengan pH 7,8; dan kelompok kontrol tidak dilakukan perendaman. Kekerasan sampel diukur menggunakan Vickers hardness tester. Data dianalisis menggunakan uji Analysis of Variance (ANOVA). Hasil penelitian mendapatkan nilai rerata dan standar deviasi (SD) kekerasan resin komposit bulk-fill pada kelompok kontrol, kelompok I, II dan II ialah 63,933±4,721 VHN, 63,233±3,518 VHN, 64,683±7,600 VHN, dan 69,267±12,545 VHN secara berurut. Hasil tersebut menunjukkan bahwa terjadi penurunan kekerasan pada kelompok I dan terjadi peningkatan kekerasan pada kelompok II dan III. Uji ANOVA menunjukkan bahwa tidak terdapat perbedaan bermakna pada semua kelompok dengan nilai p 0,474 (p>0,05). Simpulan penelitian ini ialah variasi pH saliva tidak berpengaruh secara bermakna terhadap kekerasan resin komposit bulk-fill. Kata kunci: pH saliva; resin komposit bulk-fill; kekerasan resin
摘要:复合树脂是目前应用最广泛的牙科修复材料。填充物会一直与口腔中的唾液接触。本研究旨在确定唾液pH值变化对体填充复合树脂硬度的影响。这是一项仅采用对照组设计的后测实验研究。样品由28个直径为8mm,厚度为4mm的大块填充复合树脂样品组成。将样品分为四组:第一组,浸泡在pH为5.3的唾液中;II组,浸泡在pH为6.6的唾液中;III组,浸泡在pH为7.8的唾液中;另一组是对照组,没有接受治疗。用维氏硬度计测定试样的硬度。数据分析采用方差分析(ANOVA)检验。结果表明:对照组、I组、II组和II组的硬度平均值和标准差分别为63.933±4.721 VHN、63.233±3.518 VHN、64.683±7.600 VHN和69.267±12.545 VHN。结果表明,第1组硬度降低,第2组和第3组硬度升高。方差分析显示,各组间差异无统计学意义,p值为0.474 (p>0.05)。综上所述,唾液pH值的变化对体填充复合树脂的硬度影响不显著。关键词:唾液pH值;大块填充复合树脂;摘要:树脂复合材料merupakan bahan restorasi dibidang kedokteran gigi yang paling banyak digunakan。东巴坦杨telah diapplikasikan akan selalu berkontak dengan唾液杨terdapat di rongga mulut。土娟penelitian ini ialah untuk mengetahui pengaruh variasi pH唾液terhadap kekerasan树脂复合填料。Jenis penelitian ialah实验只采用对照组设计。样品penelitian terdiri dari 28样品树脂堆肥块状填充物直径8 mm丹汀基4 mm,阳迪巴吉门贾迪帕特克龙柏,yitu:克龙柏I direndam帕达唾液登干pH 5、3;龙珠II迪伦丹帕达唾液登干pH值6,6;kelompok III direndam pada唾液登干pH 7,8;丹克罗布克控制得很好。克克拉山样品diukur menggunakan维氏硬度计。数据分析:方差分析(ANOVA)。Hasil penelitian mendapatkan nilai reata dan standar deviasi (SD) kekerasan树脂块状填料paada kelompok对照,kelompok I, II, II, 63,933±4,721 VHN, 63,233±3,518 VHN, 64,683±7,600 VHN, 69,267±12,545 VHN secara berurut。Hasil tersebut menunjukkan bahwa terjadi penurunan kekerasan pada kelompok I dan terjadi peningkatan kekerasan pada kelompok II dan III。Uji ANOVA menunjukkan bahwa tidak terdapat perbedaan bermakna pada semua kelompok dengan nilai p 0.0474 (p> 2005)。猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃、猕猴桃等。Kata kunci: pH唾液;树脂堆肥散装填料;kekerasan树脂