Study on Electrochemical Performance of Dimensionally Stable Anodes during Zinc Electrowinning

Abstract

in zinc electrowinning, small amounts of manganese ions additives are needed in the electrolyte to reduce the corrosion of anodes and minimize the contamination of cathodic zinc by dissolved lead. however, excess manganese oxide could cover the dimensionally stable anodes (DSa) surface and decrease their service life. additives of phosphoric acid are put in the electrolyte to complex the manganic Mn 3+ ion and hence reduce its disproportionation to Mno 2 . in the investigation, phosphoric acid was added to sulfuric acid or zinc electrolytes, and conventional and recent electrochemical measurements were carried out to examine electrochemical behaviour of DSa (Ti/iro 2 -Ta 2 o 5 ) anode during zinc electrolysis at 48 ma/cm 2 and 39°c. it was observed that the anodic potentials of DSa anodes were lower by 27 mV after 5 h polarization in the zinc electrolyte containing 35 g/l phosphoric acid at 39°c. Electrochemical impedance measurements show that the addition of 35 ml/l h 3 Po 4 to the zinc electrolyte can increase impedance resistances of the DSa mesh anodes. cyclic voltammogram studies (cV) at a scan rate of 5 mV/s without agitation show that the oxidation peak in the solution with 35 ml/l phosphoric acid addition is highest, followed by that with 17 ml/l phosphoric acid addition and that without addition of phosphoric acid.