Sintesis Zeolit, Y. Dari, Lumpur Lapindo, Dengan Variasi, Keterisian Autoklaf, dan Variasi, Rasio Molar, SiAl, Novita Andarini, Deys Sya’fatul Maziyyah, T. Haryati, Yudi Aris Sulistiyo
{"title":"Synthesis Zeolite Y From Lapindo Mud With Variations Filling Autoclave And Ratio Molar Si/Al","authors":"Sintesis Zeolit, Y. Dari, Lumpur Lapindo, Dengan Variasi, Keterisian Autoklaf, dan Variasi, Rasio Molar, SiAl, Novita Andarini, Deys Sya’fatul Maziyyah, T. Haryati, Yudi Aris Sulistiyo","doi":"10.19184/bst.v11i3.39422","DOIUrl":null,"url":null,"abstract":"Lapindo mud contains Silicate (SiO2), and Aluminum oxide (Al2O3) that can be utilized to synthesize zeolite Y. Zeolite Y was synthesized from Lapindo mud via the smelting and hydrothermal method, respectively. The thermal activation of Lapindo mud was achieved by leaching smelting at 550oC for 2 hours with NaOH to achieve thed desire adding SiO2, NaOH and aging for 48 hours. The effects of various parameters on the synthesis were investigated. The samples were characterized with X-ray Fluorescence (XRF), X-Ray Diffraction (XRD), Fourier Transformation Infrared Spectroscopy (FTIR) and Gas Sorption Analyzer (GSA). Zeolite Y with high crystallinity was synthesized under optimized conditions, such as filling autoclave 90% and a SiO2/ Al2O3 molar ratio of 15.","PeriodicalId":353803,"journal":{"name":"BERKALA SAINSTEK","volume":"93 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2023-09-30","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"BERKALA SAINSTEK","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.19184/bst.v11i3.39422","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
Lapindo mud contains Silicate (SiO2), and Aluminum oxide (Al2O3) that can be utilized to synthesize zeolite Y. Zeolite Y was synthesized from Lapindo mud via the smelting and hydrothermal method, respectively. The thermal activation of Lapindo mud was achieved by leaching smelting at 550oC for 2 hours with NaOH to achieve thed desire adding SiO2, NaOH and aging for 48 hours. The effects of various parameters on the synthesis were investigated. The samples were characterized with X-ray Fluorescence (XRF), X-Ray Diffraction (XRD), Fourier Transformation Infrared Spectroscopy (FTIR) and Gas Sorption Analyzer (GSA). Zeolite Y with high crystallinity was synthesized under optimized conditions, such as filling autoclave 90% and a SiO2/ Al2O3 molar ratio of 15.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们