{"title":"Additive manufacturing to design a new material TiB2-reinforced SUS316L using TiB2-Fe composite powder","authors":"R. Otsuka, T. Kikuchi, T. Yamamoto, S. Katayama","doi":"10.1088/1757-899x/1310/1/012002","DOIUrl":null,"url":null,"abstract":"The metal additive manufacturing (AM) process allows for the production of three-dimensional (3D) parts with unique geometries that could not be formed by conventional methods. However, our aim is to utilize the AM process to create never-before-seen new materials because we believe it holds potential not only for new processing but also for creating a new material. The TiB<sub>2</sub>-Fe composite powder developed as a new raw material of the AM process, which was used as an additive powder in additive manufactured (AMed) SUS316L for effectively improving the mechanical properties of AMed SUS316L. The TiB<sub>2</sub>-reinfoced SUS316L synthesized by a Powder Bed Fusion (PBF) method using the TiB<sub>2</sub>-Fe composite powder had an extremely high Vickers hardness and strength of about 400 HV and 1250 MPa, respectively, being close to twice those of AMed SUS316L.","PeriodicalId":14483,"journal":{"name":"IOP Conference Series: Materials Science and Engineering","volume":"65 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2024-08-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"IOP Conference Series: Materials Science and Engineering","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1088/1757-899x/1310/1/012002","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
The metal additive manufacturing (AM) process allows for the production of three-dimensional (3D) parts with unique geometries that could not be formed by conventional methods. However, our aim is to utilize the AM process to create never-before-seen new materials because we believe it holds potential not only for new processing but also for creating a new material. The TiB2-Fe composite powder developed as a new raw material of the AM process, which was used as an additive powder in additive manufactured (AMed) SUS316L for effectively improving the mechanical properties of AMed SUS316L. The TiB2-reinfoced SUS316L synthesized by a Powder Bed Fusion (PBF) method using the TiB2-Fe composite powder had an extremely high Vickers hardness and strength of about 400 HV and 1250 MPa, respectively, being close to twice those of AMed SUS316L.