{"title":"Effect of Impact Energy on the Interface Microstructure of Explosively Clad Mild Steel and Titanium","authors":"T. N. Prasanthi, P. K. Parida, Ravikirana, R. Mythili, C. Sudha","doi":"10.1007/s12666-024-03449-y","DOIUrl":null,"url":null,"abstract":"<p>Effect of load ratio (<i>R</i>) on the interface microstructure and phase stability was investigated in mild steel/Grade-2 Ti explosive clads using experimental and JMatPro® computations. At low-impact-energy conditions (i.e., <i>R</i> = 1.07), the interface exhibited a symmetrical wavy morphology with molten metal entrapped in isolated regions within the vortices of the waves, while at high-impact loading conditions (<i>R</i> = 3) the interface had complex weld solidification structure consisting of planar interface, columnar and equiaxed dendrites. Based on the study, it was concluded that under high-impact loading conditions, the interface microstructure of the explosive clads will resemble fusion welded joints, but with relatively lower thickness of the interaction zones.</p>","PeriodicalId":23224,"journal":{"name":"Transactions of The Indian Institute of Metals","volume":"3 1","pages":""},"PeriodicalIF":1.6000,"publicationDate":"2024-09-12","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Transactions of The Indian Institute of Metals","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1007/s12666-024-03449-y","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"Materials Science","Score":null,"Total":0}
引用次数: 0
Abstract
Effect of load ratio (R) on the interface microstructure and phase stability was investigated in mild steel/Grade-2 Ti explosive clads using experimental and JMatPro® computations. At low-impact-energy conditions (i.e., R = 1.07), the interface exhibited a symmetrical wavy morphology with molten metal entrapped in isolated regions within the vortices of the waves, while at high-impact loading conditions (R = 3) the interface had complex weld solidification structure consisting of planar interface, columnar and equiaxed dendrites. Based on the study, it was concluded that under high-impact loading conditions, the interface microstructure of the explosive clads will resemble fusion welded joints, but with relatively lower thickness of the interaction zones.
期刊介绍：
Transactions of the Indian Institute of Metals publishes original research articles and reviews on ferrous and non-ferrous process metallurgy, structural and functional materials development, physical, chemical and mechanical metallurgy, welding science and technology, metal forming, particulate technologies, surface engineering, characterization of materials, thermodynamics and kinetics, materials modelling and other allied branches of Metallurgy and Materials Engineering.
Transactions of the Indian Institute of Metals also serves as a forum for rapid publication of recent advances in all the branches of Metallurgy and Materials Engineering. The technical content of the journal is scrutinized by the Editorial Board composed of experts from various disciplines of Metallurgy and Materials Engineering. Editorial Advisory Board provides valuable advice on technical matters related to the publication of Transactions.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们