Effect of cryogenic temperature on the strengthening mechanisms of AZ61 Mg alloy extruded at different temperatures

IF 6.2 2区 材料科学 Q1 MATERIALS SCIENCE, MULTIDISCIPLINARY Journal of Materials Research and Technology-Jmr&t Pub Date : 2024-09-11 DOI:10.1016/j.jmrt.2024.09.068
Hafiz Muhammad Rehan Tariq , Umer Masood Chaudry , Joung Sik Suh , Young Min Kim , Tea-Sung Jun
{"title":"Effect of cryogenic temperature on the strengthening mechanisms of AZ61 Mg alloy extruded at different temperatures","authors":"Hafiz Muhammad Rehan Tariq ,&nbsp;Umer Masood Chaudry ,&nbsp;Joung Sik Suh ,&nbsp;Young Min Kim ,&nbsp;Tea-Sung Jun","doi":"10.1016/j.jmrt.2024.09.068","DOIUrl":null,"url":null,"abstract":"<div><p>This study investigates the influence of extrusion and deformation temperatures on the mechanical properties of the AZ61 Mg alloy. Increasing the extrusion temperature from 300 to 400 °C led to larger grain size and higher basal texture intensity. At 400 °C, the AZ61 alloy exhibited more Al–Mn phases and fewer Mg<sub>17</sub>Al<sub>12</sub> phases, indicating enhanced dissolution of Mg<sub>17</sub>Al<sub>12</sub> in the α-Mg matrix. Uniaxial tensile tests were conducted at room temperature (RT) and cryogenic temperature (CT, −150 °C). Despite grain growth, a higher yield strength (YS) was achieved at higher extrusion temperatures due to the texture-strengthening mechanism. However, during deformation at CT, the higher YS was primarily attributed to the formation of multiple twinning within individual grains, causing twinning interactions. These twin-interacting boundaries create additional barriers to dislocation movement. Notably, the AZ61 sample extruded at 400 °C demonstrated the formation of stacking faults during deformation at CT, with dislocations accumulating around the faults. This contributed to the best strength without compromising ductility in this sample.</p></div>","PeriodicalId":54332,"journal":{"name":"Journal of Materials Research and Technology-Jmr&t","volume":"33 ","pages":"Pages 335-348"},"PeriodicalIF":6.2000,"publicationDate":"2024-09-11","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.sciencedirect.com/science/article/pii/S2238785424020738/pdfft?md5=7c125b699f14e339e273d041769c68e3&pid=1-s2.0-S2238785424020738-main.pdf","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Materials Research and Technology-Jmr&t","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S2238785424020738","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0

Abstract

This study investigates the influence of extrusion and deformation temperatures on the mechanical properties of the AZ61 Mg alloy. Increasing the extrusion temperature from 300 to 400 °C led to larger grain size and higher basal texture intensity. At 400 °C, the AZ61 alloy exhibited more Al–Mn phases and fewer Mg17Al12 phases, indicating enhanced dissolution of Mg17Al12 in the α-Mg matrix. Uniaxial tensile tests were conducted at room temperature (RT) and cryogenic temperature (CT, −150 °C). Despite grain growth, a higher yield strength (YS) was achieved at higher extrusion temperatures due to the texture-strengthening mechanism. However, during deformation at CT, the higher YS was primarily attributed to the formation of multiple twinning within individual grains, causing twinning interactions. These twin-interacting boundaries create additional barriers to dislocation movement. Notably, the AZ61 sample extruded at 400 °C demonstrated the formation of stacking faults during deformation at CT, with dislocations accumulating around the faults. This contributed to the best strength without compromising ductility in this sample.

查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
低温对不同温度下挤压成型的 AZ61 镁合金强化机制的影响
本研究探讨了挤压和变形温度对 AZ61 镁合金机械性能的影响。将挤压温度从 300°C 提高到 400°C,可使晶粒尺寸增大,基底纹理强度提高。400 °C时,AZ61合金显示出更多的Al-Mn相和更少的Mg17Al12相,这表明α-镁基体中Mg17Al12的溶解增强。在室温(RT)和低温(CT,-150 °C)下进行了单轴拉伸试验。尽管存在晶粒生长,但由于质地强化机制,在较高的挤压温度下获得了较高的屈服强度(YS)。然而,在 CT 变形过程中,较高的 YS 主要归因于单个晶粒内形成了多个孪晶,导致孪晶相互作用。这些孪晶相互作用边界为位错运动提供了额外的障碍。值得注意的是,在 400 °C 下挤压的 AZ61 样品在 CT 变形过程中形成了堆积断层,位错在断层周围聚集。这使得该样品在不影响延展性的情况下获得了最佳强度。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
Journal of Materials Research and Technology-Jmr&t
Journal of Materials Research and Technology-Jmr&t Materials Science-Metals and Alloys
CiteScore
8.80
自引率
9.40%
发文量
1877
审稿时长
35 days
期刊介绍: The Journal of Materials Research and Technology is a publication of ABM - Brazilian Metallurgical, Materials and Mining Association - and publishes four issues per year also with a free version online (www.jmrt.com.br). The journal provides an international medium for the publication of theoretical and experimental studies related to Metallurgy, Materials and Minerals research and technology. Appropriate submissions to the Journal of Materials Research and Technology should include scientific and/or engineering factors which affect processes and products in the Metallurgy, Materials and Mining areas.
期刊最新文献
Investigation of the impact of process parameters and thermal treatments on mechanical properties and microstructure of ScanCromAl ® manufactured via powder bed fusion laser beam process A novel high-Mn duplex twinning-induced plasticity lightweight steel with high yield strength and large ductility Influence of laser absorptivity of CuCr0.8 substrate surface state on the characteristics of laser directed energy deposition inconel 718 single track Additively manufactured FeCoNiSi0.2 alloy with excellent soft magnetic and mechanical properties through texture engineering Experimental study on the ballistic performance of CFRP/AFB sandwich plate
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1