{"title":"Investigation of the high temperature molten salt corrosion properties of Inconel625 alloy with Al","authors":"","doi":"10.1016/j.matchar.2024.114397","DOIUrl":null,"url":null,"abstract":"<div><div>The Inconel625 (In625) alloy is one of the main materials in heat receivers of concentrated solar power (CSP). To further improve the corrosion resistance of heat receivers in molten salt, Al element that can form an oxide film was added into In625 alloy. In this study, In625 alloy with 3 wt% Al was prepared, and its corrosion resistance in carbonate (Li<sub>2</sub>CO<sub>3</sub>-Na<sub>2</sub>CO<sub>3</sub>-K<sub>2</sub>CO<sub>3</sub>) at 650 °C was studied. Results showed that a continuous dense oxide protective film (Al<sub>2</sub>O<sub>3</sub> + LiAlO<sub>2</sub>) in surface of sample was formed by adding Al element during high temperature molten salt corrosion, which reduced the corrosion rate of In625 alloy. The corrosion rate of In625 alloy with 3 wt% Al corroded for 48 h and 120 h were 44 μm/year and 89 μm/year, respectively.</div></div>","PeriodicalId":18727,"journal":{"name":"Materials Characterization","volume":null,"pages":null},"PeriodicalIF":4.8000,"publicationDate":"2024-09-20","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Characterization","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S1044580324007782","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"MATERIALS SCIENCE, CHARACTERIZATION & TESTING","Score":null,"Total":0}
引用次数: 0
Abstract
The Inconel625 (In625) alloy is one of the main materials in heat receivers of concentrated solar power (CSP). To further improve the corrosion resistance of heat receivers in molten salt, Al element that can form an oxide film was added into In625 alloy. In this study, In625 alloy with 3 wt% Al was prepared, and its corrosion resistance in carbonate (Li2CO3-Na2CO3-K2CO3) at 650 °C was studied. Results showed that a continuous dense oxide protective film (Al2O3 + LiAlO2) in surface of sample was formed by adding Al element during high temperature molten salt corrosion, which reduced the corrosion rate of In625 alloy. The corrosion rate of In625 alloy with 3 wt% Al corroded for 48 h and 120 h were 44 μm/year and 89 μm/year, respectively.
期刊介绍：
Materials Characterization features original articles and state-of-the-art reviews on theoretical and practical aspects of the structure and behaviour of materials.
The Journal focuses on all characterization techniques, including all forms of microscopy (light, electron, acoustic, etc.,) and analysis (especially microanalysis and surface analytical techniques). Developments in both this wide range of techniques and their application to the quantification of the microstructure of materials are essential facets of the Journal.
The Journal provides the Materials Scientist/Engineer with up-to-date information on many types of materials with an underlying theme of explaining the behavior of materials using novel approaches. Materials covered by the journal include:
Metals & Alloys
Ceramics
Nanomaterials
Biomedical materials
Optical materials
Composites
Natural Materials.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们