Investigation of Titanium Nitride as an Effective Interphase for Carbon-Fiber-Reinforced Silicon Carbide Ceramic Matrix Composites.

Abstract

Ceramic matrix composites (CMCs) have played a significant role in increasing the efficiency of gas turbine engines. CMCs combine the high temperature resistance of ceramics with the high mechanical strength of ceramic fibers into a single unit. Interphase layers are a crucial component in CMCs, as they prevent ceramic fibers from oxidation and introduce strengthening mechanisms into the composite. Hexagonal boron nitride and pyrolytic carbon are the most commonly used interphase layers in the aerospace industry. Other than that, very few materials have been evaluated as interphase layers. In this study, we explore the possibilities of using titanium nitride as an interphase layer in single-tow CMCs (mini composite) representative of a unidirectional composite at a smaller scale. T-300 carbon fibers were coated with TiN by atmospheric pressure chemical vapor infiltration using TiCl₄, N₂, and H₂. The deposition temperature, precursor flow rate ratio, total precursor flow rate, and deposition time were optimized to obtain high-quality coatings. The best coating was produced at 800 °C, 4:1 H₂ [TiCl₄]/N₂ ratio, 125 standard cubic centimeters per minute (N₂ + H₂ [TiCl₄]) total flow precursor flow rate, and 2 h of deposition time. At these conditions, the coatings displayed good fiber coverage, good fiber adhesion, minimum fiber linkage, and minimum surface roughness. There was minimum fiber degradation after TiN coating, with a retention of 95% of the initial Young's modulus and 26% of the ultimate tensile strength of the carbon fiber. Adding the TiN interphase coating to the Cf/SiC CMC increased the ultimate tensile strength of the composite by 1122% and Young's modulus by 150%.