Influence of sintering process on high temperature cyclic deformation behavior and fatigue creep damage mechanism of sintered silver

IF 5.7 2区材料科学 Q1 ENGINEERING, MECHANICAL International Journal of Fatigue Pub Date : 2025-01-26 DOI:10.1016/j.ijfatigue.2025.108839

Dao-Hang Li , Wen-Jing Xu , Tian-Yi Liu , Bowen Zhang , Yi Liu , Yun-Hui Mei

引用次数: 0

Abstract

In this paper, the influence of sintering process on the high temperature cyclic deformation behavior and fatigue creep damage mechanism of sintered silver is revealed. Under cyclic shear loading at high temperatures, quasi cleavage fracture that symbolizes creep damage is induced in sintered silver, leading to a decrease in its fatigue life. With the increase of sintering temperature/time, the material properties of sintered silver are enhanced by improving sintering quality, including a decrease in porosity, an increase in grain size, an increase in shear strength, an increase in fatigue life, and a decrease in shear strain amplitude response.

查看原文

微信好友朋友圈 QQ好友复制链接

本刊更多论文

求助全文

约1分钟内获得全文去求助

来源期刊

International Journal of Fatigue 工程技术-材料科学：综合

CiteScore

10.70

自引率

21.70%

发文量

619

审稿时长

58 days

期刊介绍： Typical subjects discussed in International Journal of Fatigue address: Novel fatigue testing and characterization methods (new kinds of fatigue tests, critical evaluation of existing methods, in situ measurement of fatigue degradation, non-contact field measurements) Multiaxial fatigue and complex loading effects of materials and structures, exploring state-of-the-art concepts in degradation under cyclic loading Fatigue in the very high cycle regime, including failure mode transitions from surface to subsurface, effects of surface treatment, processing, and loading conditions Modeling (including degradation processes and related driving forces, multiscale/multi-resolution methods, computational hierarchical and concurrent methods for coupled component and material responses, novel methods for notch root analysis, fracture mechanics, damage mechanics, crack growth kinetics, life prediction and durability, and prediction of stochastic fatigue behavior reflecting microstructure and service conditions) Models for early stages of fatigue crack formation and growth that explicitly consider microstructure and relevant materials science aspects Understanding the influence or manufacturing and processing route on fatigue degradation, and embedding this understanding in more predictive schemes for mitigation and design against fatigue Prognosis and damage state awareness (including sensors, monitoring, methodology, interactive control, accelerated methods, data interpretation) Applications of technologies associated with fatigue and their implications for structural integrity and reliability. This includes issues related to design, operation and maintenance, i.e., life cycle engineering Smart materials and structures that can sense and mitigate fatigue degradation Fatigue of devices and structures at small scales, including effects of process route and surfaces/interfaces.