Optical Properties of Newly Developed Monolithic CAD/CAM Materials After Aging

IF 0.3 Q4 MEDICINE, RESEARCH & EXPERIMENTAL Clinical and Experimental Health Sciences Pub Date : 2023-01-17 DOI:10.33808/clinexphealthsci.1185717
Hatice Banu UYSAL ÖZEL, Yılmaz Umut Aslan, Erkan Sancakli
{"title":"Optical Properties of Newly Developed Monolithic CAD/CAM Materials After Aging","authors":"Hatice Banu UYSAL ÖZEL, Yılmaz Umut Aslan, Erkan Sancakli","doi":"10.33808/clinexphealthsci.1185717","DOIUrl":null,"url":null,"abstract":"Objective: With the widespread use of CAD/CAM (computer aided design and manufacture) systems in dentistry, many restorative materials have been produced. In our study, we aimed to evaluate the change in optical properties of newly developed translucent monolithic zirconia (TMZ) (Cercon HT Dentsply, Sirona, USA), zirconia-reinforced lithium silicate (ZLS) (Celtra Duo, Dentsply, Germany) and lithium disilicate (LS2) (IPS e.max CAD, Ivoclar Vivadent, Liechtenstein) materials with aging. \nMethods:10 discs of 12mm diameter and 1.2 mm thickness were produced from high translucent A2 color of each material. The aging process was applied in an autoclave under 134ºC, 0.2MPa pressure. For optical evaluation, L*, a*, b* values of the samples were measured by spectrophotometry before aging, after 3 hours and 6 hours aging. ΔE00 values and translucency parameters (TP) were calculated. The data were evaluated statistically. \nResults: In the present study, all the materials had undergone color change as a result of aging, but this change was within acceptable limits (ΔE00 0.8). There was a decrease in the translucency of all materials used in the study, but this decrease was not statistically significant. \nConclusion: In the light of the findings obtained from this in vitro study, aging did not cause color and translucency changes in TMZ, ZLS, LS2 monolithic CAD/CAM materials.","PeriodicalId":10192,"journal":{"name":"Clinical and Experimental Health Sciences","volume":null,"pages":null},"PeriodicalIF":0.3000,"publicationDate":"2023-01-17","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Clinical and Experimental Health Sciences","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.33808/clinexphealthsci.1185717","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MEDICINE, RESEARCH & EXPERIMENTAL","Score":null,"Total":0}
引用次数: 0

Abstract

Objective: With the widespread use of CAD/CAM (computer aided design and manufacture) systems in dentistry, many restorative materials have been produced. In our study, we aimed to evaluate the change in optical properties of newly developed translucent monolithic zirconia (TMZ) (Cercon HT Dentsply, Sirona, USA), zirconia-reinforced lithium silicate (ZLS) (Celtra Duo, Dentsply, Germany) and lithium disilicate (LS2) (IPS e.max CAD, Ivoclar Vivadent, Liechtenstein) materials with aging. Methods:10 discs of 12mm diameter and 1.2 mm thickness were produced from high translucent A2 color of each material. The aging process was applied in an autoclave under 134ºC, 0.2MPa pressure. For optical evaluation, L*, a*, b* values of the samples were measured by spectrophotometry before aging, after 3 hours and 6 hours aging. ΔE00 values and translucency parameters (TP) were calculated. The data were evaluated statistically. Results: In the present study, all the materials had undergone color change as a result of aging, but this change was within acceptable limits (ΔE00 0.8). There was a decrease in the translucency of all materials used in the study, but this decrease was not statistically significant. Conclusion: In the light of the findings obtained from this in vitro study, aging did not cause color and translucency changes in TMZ, ZLS, LS2 monolithic CAD/CAM materials.
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
新开发的单片CAD/CAM材料老化后的光学性能
目的:随着计算机辅助设计与制造系统在牙科中的广泛应用,产生了许多修复材料。在我们的研究中,我们旨在评估新开发的半透明单片氧化锆(TMZ)(Cercon HT Dentsply,美国Sirona)、氧化锆增强硅酸锂(ZLS)(Celtra Duo,Dentspli,德国)和二硅酸锂(LS2)(IPS e.max CAD,Ivoclar Vivadent,列支敦士登)材料的光学性能随老化的变化。方法:用每种材料的高透光A2色制作10个直径12mm、厚度1.2mm的椎间盘。在134ºC、0.2MPa压力下的高压釜中进行老化处理。对于光学评价,在老化前、老化3小时和老化6小时后通过分光光度法测量样品的L*、a*、b*值。ΔE00值和半透明性参数(TP)。对数据进行了统计评估。结果:在本研究中,所有材料都因老化而发生了颜色变化,但这种变化在可接受的范围内(ΔE00 0.8)。研究中使用的所有材料的半透明性都有所下降,但这种下降没有统计学意义。结论:根据本体外研究的结果,TMZ、ZLS、LS2单片CAD/CAM材料的老化不会引起颜色和半透明性的变化。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
Clinical and Experimental Health Sciences
Clinical and Experimental Health Sciences MEDICINE, RESEARCH & EXPERIMENTAL-
自引率
0.00%
发文量
73
期刊最新文献
Presumptive Molecular Interconnections Between COVID-19 And Huntington’s Disease Enhanced Enzyme Inhibitory Effects of the Nanohybrid Eggplant Extract: An Unusual Pharmaceutical Form for Medicinal Plant The Validity and Reliability of the Postpartum Symptom Inventory in Turkish Women The Effect of Sex Education and Counseling Based on the Ex-PLISSIT Model on Sexual Life in Primigravidas Ketogenic Diet Interventions in Inborn Errors of Metabolism: A Review Article
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1