{"title":"Preparation of Transparent MgAl2O4 Spinel by Pulsed Electric Current Sintering Using Two-step Heating Method","authors":"Y. Nguyen, H. M. Le, Tu Anh Dao, H. N. Tran, T. Nguyen, Thang Hong Le, K. Dang","doi":"10.36547/ams.27.4.1212","DOIUrl":null,"url":null,"abstract":"Transparent MgAl2O4 ceramics were fabricated by pulsed electric current sintering (PECS) employing two-step sintering mode. First, nanoscale MgAl2O4 powders were produced by solution combustion synthesis from hydrated nitrate compounds and urea. Subsequently, the synthesized powders were sintered by PECS with a heating rate of 100oC/min under an applied pressure of 100 MPa. The sintering process was conducted according to two-step heating profile. At the first step, the temperature increased to 1050, 1100, and 1150oC, followed by a dwell time of 60 min. The second-step sintering was carried out at 1300, 1350, and 1400oC for 20 min. The transparent ceramics sintered at 1050oC/ 60 min – 1400oC/ 20 min exhibited transmittance over 80% in infrared range. In addition, transparent samples presented a Vickers hardness up to 30 GPa for sintering mode of 1150oC/ 60 min – 1400oC/ 20 min.","PeriodicalId":44511,"journal":{"name":"Acta Metallurgica Slovaca","volume":" ","pages":""},"PeriodicalIF":1.1000,"publicationDate":"2021-12-07","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Acta Metallurgica Slovaca","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.36547/ams.27.4.1212","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
引用次数: 1
Abstract
Transparent MgAl2O4 ceramics were fabricated by pulsed electric current sintering (PECS) employing two-step sintering mode. First, nanoscale MgAl2O4 powders were produced by solution combustion synthesis from hydrated nitrate compounds and urea. Subsequently, the synthesized powders were sintered by PECS with a heating rate of 100oC/min under an applied pressure of 100 MPa. The sintering process was conducted according to two-step heating profile. At the first step, the temperature increased to 1050, 1100, and 1150oC, followed by a dwell time of 60 min. The second-step sintering was carried out at 1300, 1350, and 1400oC for 20 min. The transparent ceramics sintered at 1050oC/ 60 min – 1400oC/ 20 min exhibited transmittance over 80% in infrared range. In addition, transparent samples presented a Vickers hardness up to 30 GPa for sintering mode of 1150oC/ 60 min – 1400oC/ 20 min.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们