Microstructure and mechanical properties of Ti3SiC2 MAX phases sintered by hot pressing

Sheida Haji Amiri, Nasser Pourmohammadie Vafa
{"title":"Microstructure and mechanical properties of Ti3SiC2 MAX phases sintered by hot pressing","authors":"Sheida Haji Amiri, Nasser Pourmohammadie Vafa","doi":"10.53063/synsint.2021.1472","DOIUrl":null,"url":null,"abstract":"The Ti3SiC2 used in this project has been purchased ready-made. This study aimed to investigate the effect of sintering temperature on samples' microstructure and mechanical properties, including three-point flexural strength, Vickers hardness, and fracture toughness. Therefore, Ti3SiC2 samples were sintered under a vacuum atmosphere at a pressure of 35 MPa for 30 minutes at two temperatures of 1500 °C and 1550 °C by hot pressing. The microstructure obtained from the fracture cross-section of the samples shows that by increasing the sintering temperature to 1550 °C, the microstructure of this sample becomes larger than the sintered sample at 1500 °C. Also, increasing the sintering temperature to 1550 °C causes the decomposition of Ti3SiC2 to TiC, which can be seen in the X-ray diffraction pattern (XRD). In addition, the relative density of the sintered sample at 1550 °C is 98.08% which is higher than that of the sintered sample at 1500 °C with the result of 89%. On the other hand, the three-point flexural strength (227.5 MPa), the Vickers hardness (~9 GPa), and the fracture toughness (8.6 MPa.m1/2) of the sintered sample at 1500 °C are higher due to the fine-grained structure.","PeriodicalId":22113,"journal":{"name":"Synthesis and Sintering","volume":"68 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2021-12-27","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"2","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Synthesis and Sintering","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.53063/synsint.2021.1472","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 2

Abstract

The Ti3SiC2 used in this project has been purchased ready-made. This study aimed to investigate the effect of sintering temperature on samples' microstructure and mechanical properties, including three-point flexural strength, Vickers hardness, and fracture toughness. Therefore, Ti3SiC2 samples were sintered under a vacuum atmosphere at a pressure of 35 MPa for 30 minutes at two temperatures of 1500 °C and 1550 °C by hot pressing. The microstructure obtained from the fracture cross-section of the samples shows that by increasing the sintering temperature to 1550 °C, the microstructure of this sample becomes larger than the sintered sample at 1500 °C. Also, increasing the sintering temperature to 1550 °C causes the decomposition of Ti3SiC2 to TiC, which can be seen in the X-ray diffraction pattern (XRD). In addition, the relative density of the sintered sample at 1550 °C is 98.08% which is higher than that of the sintered sample at 1500 °C with the result of 89%. On the other hand, the three-point flexural strength (227.5 MPa), the Vickers hardness (~9 GPa), and the fracture toughness (8.6 MPa.m1/2) of the sintered sample at 1500 °C are higher due to the fine-grained structure.
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
热压烧结Ti3SiC2 MAX相的组织与力学性能
本项目所使用的Ti3SiC2材料是购买的现成材料。本研究旨在研究烧结温度对试样显微组织和力学性能的影响,包括三点抗弯强度、维氏硬度和断裂韧性。因此,采用热压法在1500℃和1550℃两个温度下,在压力为35 MPa的真空气氛下烧结Ti3SiC2样品30分钟。试样断口断面的显微组织表明,将烧结温度提高到1550℃后,试样的显微组织比1500℃时的烧结试样大。同时,将烧结温度提高到1550℃时,Ti3SiC2分解为TiC,这在x射线衍射图(XRD)中可以看出。1550℃烧结试样的相对密度为98.08%,高于1500℃烧结试样的89%。另一方面,烧结试样在1500℃时的三点抗弯强度(227.5 MPa)、维氏硬度(~9 GPa)和断裂韧性(8.6 MPa.m1/2)均因其细晶组织而提高。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
自引率
0.00%
发文量
0
期刊最新文献
3D-printed calcium magnesium silicates: A mini-review Solid-solution phase formation rules for high entropy alloys: A thermodynamic perspective A review of synthesis strategies for nickel cobaltite-based composites in supercapacitor applications Synthesis and doping of high-temperature resistant spinel nano pigments: A review Effects of die geometry and insulation on the energy and electrical parameters analyses of spark plasma sintered TiC ceramics
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1