{"title":"Hydroxyapatite Matrix Composites by Hot Isostatic Pressing: Part 2. Zirconia Fibre and Powder Reinforced","authors":"N. Ehsani, C. Sorrell, A. Ruys","doi":"10.4028/www.scientific.net/JBBTE.15.85","DOIUrl":null,"url":null,"abstract":"The Aim of the Project Was to Enhance the Fracture Toughness of Hydroxyapatite to a Level Comparable to that of Natural Bone for in Vivo Applications. to this Aim, the Effect of Various Parameters, Were Studied. Fully Dense Decomposition-Free Hap Matrix Composite Was Produced Using Hot Isostatic Pressing Technique. A Graphite/stainless Steel Encapsulation System Was Found to Be an Appropriate Method. Glass Encapsulation Was Unsuccessful Technique due to the Excessive Low-Temperature Volatilisation, which Aerated the Glass. Toughness Improvement Was 2.7 Times for PSZ Fibres, and 2.4 Times for PSZ Powder. the Optimal Addition Level of PSZ Fibre and PSZ Powder Was 20 Vol% and ~30 Vol% Respectively. Further, it Was Found that the Hap Decomposition Temperature Was Higher at 100 Mpa (the Hiping Pressure) than for Pressureless Sintering. the Toughening Effect of the Additives Induced Plastic Deformation and Ductile Fracture.","PeriodicalId":15198,"journal":{"name":"Journal of Biomimetics, Biomaterials and Tissue Engineering","volume":"18 1","pages":"100 - 85"},"PeriodicalIF":0.0000,"publicationDate":"2012-10-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"3","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Biomimetics, Biomaterials and Tissue Engineering","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.4028/www.scientific.net/JBBTE.15.85","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 3
Abstract
The Aim of the Project Was to Enhance the Fracture Toughness of Hydroxyapatite to a Level Comparable to that of Natural Bone for in Vivo Applications. to this Aim, the Effect of Various Parameters, Were Studied. Fully Dense Decomposition-Free Hap Matrix Composite Was Produced Using Hot Isostatic Pressing Technique. A Graphite/stainless Steel Encapsulation System Was Found to Be an Appropriate Method. Glass Encapsulation Was Unsuccessful Technique due to the Excessive Low-Temperature Volatilisation, which Aerated the Glass. Toughness Improvement Was 2.7 Times for PSZ Fibres, and 2.4 Times for PSZ Powder. the Optimal Addition Level of PSZ Fibre and PSZ Powder Was 20 Vol% and ~30 Vol% Respectively. Further, it Was Found that the Hap Decomposition Temperature Was Higher at 100 Mpa (the Hiping Pressure) than for Pressureless Sintering. the Toughening Effect of the Additives Induced Plastic Deformation and Ductile Fracture.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们