{"title":"Alkali Treatment to Maximize Adhesion of Polypyrrole Coatings for Electro-Conductive Textile Materials","authors":"Z. Yildiz","doi":"10.30564/opmr.v1i1.1010","DOIUrl":null,"url":null,"abstract":"In this paper polyester fabrics were pretreated with alkaline solution to improve the ability for the fabric surface to bond with polypyrrole (PPy) coating layer. In situ chemical oxidative polymerization of pyrrole monomer was performed on alkali treated polyester fabrics. Then the fabrics were characterized by FTIR and XRD analysis. The tensile properties of the yarns in both warp and weft directions were measured after alkali treatment and PPy coating processes. The abrasion resistance test was performed on PPy coated fabrics with and without alkali treatment. The surface electrical resistivity of PPy coated fabrics were searched. The electromagnetic shielding effectiveness (EMSE) properties of fabrics in terms of reflection, absorption and transmission behaviors were also investigated. A significant EMSE value increase (about 27%) was obtained with alkali treatment.","PeriodicalId":19583,"journal":{"name":"Organic Polymer Material Research","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2019-10-31","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Organic Polymer Material Research","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.30564/opmr.v1i1.1010","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 1
Abstract
In this paper polyester fabrics were pretreated with alkaline solution to improve the ability for the fabric surface to bond with polypyrrole (PPy) coating layer. In situ chemical oxidative polymerization of pyrrole monomer was performed on alkali treated polyester fabrics. Then the fabrics were characterized by FTIR and XRD analysis. The tensile properties of the yarns in both warp and weft directions were measured after alkali treatment and PPy coating processes. The abrasion resistance test was performed on PPy coated fabrics with and without alkali treatment. The surface electrical resistivity of PPy coated fabrics were searched. The electromagnetic shielding effectiveness (EMSE) properties of fabrics in terms of reflection, absorption and transmission behaviors were also investigated. A significant EMSE value increase (about 27%) was obtained with alkali treatment.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们