Influence of sulfate-reducing bacteria on the biocorrosion of mild steel coated with hybrid polyetherimide-ZnO or CuO bilayer composites

Mild steel (MS) coated with protective bilayer hybrid coatings of polyetherimide, and ZnO/CuO was exposed to artificial treated wastewater (ATWW) inoculated with Desulfovibrio sp. (biotic system). Proteins from the extracellular polymeric substances (EPS) matrix of Desulfovibrio sp. responded to the coatings. PEI-CuO offered the highest performance against biocorrosion. The higher PEI-CuO resistivity value of 2.17×10 6 Ω·cm 2 contrasted with the decrease to 1.5×10 5 and 1.6×10 3 Ω·cm 2 for PEI-ZnO and PEI coatings, respectively. The one order of magnitude increased resistance of the biotic system, compared to sterilized ATWW (abiotic system), resulted from the protective nature of the bacterial biofilm. Supplementary Materials: Supplementary material for this article is supplied as a separate file: crchim-227-suppl.pdf L’acier doux (MS) recouvert de revêtements hybrides bicouches protecteurs de polyétherimide et de ZnO/CuO a été exposé à des eaux usées artificielles (ATWW) inoculées par Desulfovibrio sp. (système biotique). Les protéines de la matrice des substances polymères extracellulaires (EPS) de Desulfovibrio sp. ont réagi aux revêtements. Le PEI-CuO a offert les meilleures performances contre la biocorrosion. La valeur de résistivité plus élevée de PEI-CuO de 2,17×10 6 Ω·cm 2 contraste avec la diminution à respectivement 1,5×10 5 et 1,6×10 3 Ω·cm 2 pour les revêtements PEI-ZnO et PEI. La résistance accrue d’un ordre de grandeur du système biotique, par rapport à l’ATWW stérilisé (système abiotique), résulte de la nature protectrice du biofilm bactérien. Compléments : Des compléments sont fournis pour cet article dans le fichier séparé : crchim-227-suppl.pdf