Reaching Large Strains During Simple Shear Experiments Thanks to Sequential Re-Machining of the Free Edges

Background

The simple shear experiment is widely used for the calibration of plasticity models due to straightforward post processing. The specimen can be as simple as a rectangular strip of sheet metal, but the maximum strain is limited by early initiation of fractures from the free edges. Avoiding this drawback has been a major motivation for the development of new specimens with optimized edge geometries or the in-plane torsion test, but at the cost of a more complex analysis of the test and often a reduction of the gauge section.

Objective

The objective of the present work is to overcome the initiation of fracture from the free edges during simple shear experiments. Our goal is to double the achievable maximum strain, while keeping the size of the specimen and the post processing simplicity of a standard simple shear test.

Methods

A sequential single shear test is proposed, consisting of several two steps sequences on a notched geometry. First, an interrupted shear test is performed up to a specified displacement value. Then, the damaged free edges of the specimen are removed through milling. The specimen is then ready for the following sequence of shear and re-machining.

Results

Experiments are performed on three engineering materials, with up to five loading-machining sequences. The maximum attained effective strain is up to two times the one reached during a monotonic experiment. Numerical simulations are used to validate the shear stress and strain calculations from experimental measurements. Practical recommendations are derived for the choice of the displacement step size and Digital Image Correlation analysis.

Conclusion

It is found that the maximum strain attained before the undesired failure of the specimen during simple shear test can be substantially extended through repeated re-machining of the specimen boundaries, enabling behavior identification at larger strains.