不同工艺制备的 NiCrAlY 金属键合层的特性和热腐蚀行为

IF 6.6 2区 材料科学 Q1 MATERIALS SCIENCE, MULTIDISCIPLINARY npj Materials Degradation Pub Date : 2024-04-09 DOI:10.1038/s41529-023-00411-z
Weiwei Qu, Zehao Chen, Zhilin Zhang, Xue Li, Fan Yang, Jinlong Wang, Minghui Chen, Shusuo Li, Fuhui Wang
{"title":"不同工艺制备的 NiCrAlY 金属键合层的特性和热腐蚀行为","authors":"Weiwei Qu, Zehao Chen, Zhilin Zhang, Xue Li, Fan Yang, Jinlong Wang, Minghui Chen, Shusuo Li, Fuhui Wang","doi":"10.1038/s41529-023-00411-z","DOIUrl":null,"url":null,"abstract":"The hot corrosion experiments of René N5 alloy coated with three different NiCrAlY metal bonding layers are carried out, that the layers are prepared by different methods (APS, HVAF and MIP). Compared with bare René N5 alloy samples, the hot corrosion resistance of coated samples is improved. It can be attributed to the small internal stress of the surface oxide layer on the coating sample, which is difficult to spall, reducing the degree of hot corrosion reaction. The hot corrosion resistance of NiCrAlY layers is MIP > HVAF > APS, which is positively positively related to the density of layers, because the influence of element diffusion in the process of hot corrosion is effectively slowed down.","PeriodicalId":19270,"journal":{"name":"npj Materials Degradation","volume":null,"pages":null},"PeriodicalIF":6.6000,"publicationDate":"2024-04-09","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.nature.com/articles/s41529-023-00411-z.pdf","citationCount":"0","resultStr":"{\"title\":\"Characteristics and hot corrosion behavior of NiCrAlY metal bonding layers prepared by different processes\",\"authors\":\"Weiwei Qu, Zehao Chen, Zhilin Zhang, Xue Li, Fan Yang, Jinlong Wang, Minghui Chen, Shusuo Li, Fuhui Wang\",\"doi\":\"10.1038/s41529-023-00411-z\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The hot corrosion experiments of René N5 alloy coated with three different NiCrAlY metal bonding layers are carried out, that the layers are prepared by different methods (APS, HVAF and MIP). Compared with bare René N5 alloy samples, the hot corrosion resistance of coated samples is improved. It can be attributed to the small internal stress of the surface oxide layer on the coating sample, which is difficult to spall, reducing the degree of hot corrosion reaction. The hot corrosion resistance of NiCrAlY layers is MIP > HVAF > APS, which is positively positively related to the density of layers, because the influence of element diffusion in the process of hot corrosion is effectively slowed down.\",\"PeriodicalId\":19270,\"journal\":{\"name\":\"npj Materials Degradation\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":6.6000,\"publicationDate\":\"2024-04-09\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://www.nature.com/articles/s41529-023-00411-z.pdf\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"npj Materials Degradation\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://www.nature.com/articles/s41529-023-00411-z\",\"RegionNum\":2,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"npj Materials Degradation","FirstCategoryId":"88","ListUrlMain":"https://www.nature.com/articles/s41529-023-00411-z","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0

摘要

通过不同的制备方法(APS、HVAF 和 MIP),对镀有三种不同 NiCrAlY 金属键合层的 René N5 合金进行了热腐蚀实验。与裸露的 René N5 合金样品相比,涂层样品的耐热腐蚀性能有所提高。这可能是因为涂层样品表面氧化层的内应力小,不易剥落,降低了热腐蚀反应的程度。NiCrAlY 涂层的耐热腐蚀性能为 MIP > HVAF > APS,与涂层密度呈正相关,这是因为在热腐蚀过程中元素扩散的影响被有效减缓了。
本文章由计算机程序翻译,如有差异,请以英文原文为准。

摘要图片

查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Characteristics and hot corrosion behavior of NiCrAlY metal bonding layers prepared by different processes
The hot corrosion experiments of René N5 alloy coated with three different NiCrAlY metal bonding layers are carried out, that the layers are prepared by different methods (APS, HVAF and MIP). Compared with bare René N5 alloy samples, the hot corrosion resistance of coated samples is improved. It can be attributed to the small internal stress of the surface oxide layer on the coating sample, which is difficult to spall, reducing the degree of hot corrosion reaction. The hot corrosion resistance of NiCrAlY layers is MIP > HVAF > APS, which is positively positively related to the density of layers, because the influence of element diffusion in the process of hot corrosion is effectively slowed down.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
npj Materials Degradation
npj Materials Degradation MATERIALS SCIENCE, MULTIDISCIPLINARY-
CiteScore
7.80
自引率
7.80%
发文量
86
审稿时长
6 weeks
期刊介绍: npj Materials Degradation considers basic and applied research that explores all aspects of the degradation of metallic and non-metallic materials. The journal broadly defines ‘materials degradation’ as a reduction in the ability of a material to perform its task in-service as a result of environmental exposure. The journal covers a broad range of topics including but not limited to: -Degradation of metals, glasses, minerals, polymers, ceramics, cements and composites in natural and engineered environments, as a result of various stimuli -Computational and experimental studies of degradation mechanisms and kinetics -Characterization of degradation by traditional and emerging techniques -New approaches and technologies for enhancing resistance to degradation -Inspection and monitoring techniques for materials in-service, such as sensing technologies
期刊最新文献
Insights into the degradation mechanism of Fe-40Ni-15Co superalloy exposed to marine atmospheric and high-temperature conditions Lifetime prediction of epoxy coating using convolutional neural networks and post processing image recognition methods Film-forming amines as corrosion inhibitors: a state-of-the-art review The effect of variable humidity on corrosion fatigue of AA7085-T7451 with surface salt deposits Unveiling the mechanism behind irregular inclusions triggering no HIC cracks in steels
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1