{"title":"氢脆对用于 FCEV 氢气阀门的 DLC 涂层机械特性的影响","authors":"Dong-Ho Shin, Seong-Jong Kim","doi":"10.1038/s41529-024-00460-y","DOIUrl":null,"url":null,"abstract":"Diamond-like carbon (DLC) coating is a surface coating technology with excellent hydrogen permeation resistance and wear resistance. However, it is difficult to completely prevent hydrogen permeation, and when hydrogen penetrates into the coating layer, the DLC coating is adversely affected. Therefore, we investigated the effect of hydrogen embrittlement on the adhesion strength and wear resistance of the DLC coating layer. As the results of the research, the surface roughness of the DLC coating was increased by a maximum of 3.8 times with hydrogen charging, and the delamination ratio of the DLC coating reached about 58%. In addition, the Lc3, which refers to the adhesion strength corresponding to the complete delamination of the DLC coating, was decreased by a maximum of 2.0 N due to hydrogen permeation. In addition, the wear resistance decreased due to hydrogen permeation, and the exposed width of the substrate due to wear increased by more than 4 times. It was also determined that hydrogen blistering or hydrogen-induced cracking occurred at the interface between the DLC coating and the chromium buffer layer due to hydrogen permeation, which decreased the durability of the DLC coating.","PeriodicalId":19270,"journal":{"name":"npj Materials Degradation","volume":" ","pages":"1-15"},"PeriodicalIF":6.6000,"publicationDate":"2024-05-04","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.nature.com/articles/s41529-024-00460-y.pdf","citationCount":"0","resultStr":"{\"title\":\"Effect of hydrogen embrittlement on mechanical characteristics of DLC-coating for hydrogen valves of FCEVs\",\"authors\":\"Dong-Ho Shin, Seong-Jong Kim\",\"doi\":\"10.1038/s41529-024-00460-y\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Diamond-like carbon (DLC) coating is a surface coating technology with excellent hydrogen permeation resistance and wear resistance. However, it is difficult to completely prevent hydrogen permeation, and when hydrogen penetrates into the coating layer, the DLC coating is adversely affected. Therefore, we investigated the effect of hydrogen embrittlement on the adhesion strength and wear resistance of the DLC coating layer. As the results of the research, the surface roughness of the DLC coating was increased by a maximum of 3.8 times with hydrogen charging, and the delamination ratio of the DLC coating reached about 58%. In addition, the Lc3, which refers to the adhesion strength corresponding to the complete delamination of the DLC coating, was decreased by a maximum of 2.0 N due to hydrogen permeation. In addition, the wear resistance decreased due to hydrogen permeation, and the exposed width of the substrate due to wear increased by more than 4 times. It was also determined that hydrogen blistering or hydrogen-induced cracking occurred at the interface between the DLC coating and the chromium buffer layer due to hydrogen permeation, which decreased the durability of the DLC coating.\",\"PeriodicalId\":19270,\"journal\":{\"name\":\"npj Materials Degradation\",\"volume\":\" \",\"pages\":\"1-15\"},\"PeriodicalIF\":6.6000,\"publicationDate\":\"2024-05-04\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://www.nature.com/articles/s41529-024-00460-y.pdf\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"npj Materials Degradation\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://www.nature.com/articles/s41529-024-00460-y\",\"RegionNum\":2,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"npj Materials Degradation","FirstCategoryId":"88","ListUrlMain":"https://www.nature.com/articles/s41529-024-00460-y","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
Effect of hydrogen embrittlement on mechanical characteristics of DLC-coating for hydrogen valves of FCEVs
Diamond-like carbon (DLC) coating is a surface coating technology with excellent hydrogen permeation resistance and wear resistance. However, it is difficult to completely prevent hydrogen permeation, and when hydrogen penetrates into the coating layer, the DLC coating is adversely affected. Therefore, we investigated the effect of hydrogen embrittlement on the adhesion strength and wear resistance of the DLC coating layer. As the results of the research, the surface roughness of the DLC coating was increased by a maximum of 3.8 times with hydrogen charging, and the delamination ratio of the DLC coating reached about 58%. In addition, the Lc3, which refers to the adhesion strength corresponding to the complete delamination of the DLC coating, was decreased by a maximum of 2.0 N due to hydrogen permeation. In addition, the wear resistance decreased due to hydrogen permeation, and the exposed width of the substrate due to wear increased by more than 4 times. It was also determined that hydrogen blistering or hydrogen-induced cracking occurred at the interface between the DLC coating and the chromium buffer layer due to hydrogen permeation, which decreased the durability of the DLC coating.
期刊介绍：
npj Materials Degradation considers basic and applied research that explores all aspects of the degradation of metallic and non-metallic materials. The journal broadly defines ‘materials degradation’ as a reduction in the ability of a material to perform its task in-service as a result of environmental exposure.
The journal covers a broad range of topics including but not limited to:
-Degradation of metals, glasses, minerals, polymers, ceramics, cements and composites in natural and engineered environments, as a result of various stimuli
-Computational and experimental studies of degradation mechanisms and kinetics
-Characterization of degradation by traditional and emerging techniques
-New approaches and technologies for enhancing resistance to degradation
-Inspection and monitoring techniques for materials in-service, such as sensing technologies
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们