{"title":"多层范德华异质结构 WS2/h-BN 的制备与摩擦学性能","authors":"Yunqi Fang, Yang Sun, Fengqin Shang, Jing Zhang, Jiayu Yao, Zihan Yan, Hangyan Shen","doi":"10.3390/lubricants12050163","DOIUrl":null,"url":null,"abstract":"Van der Waals heterostructures with incommensurate contact interfaces show excellent tribological performance, which provides solutions for the development of new solid lubricants. In this paper, a facile electrostatic layer-by-layer self-assembly (LBL) technique was proposed to prepare multi-layer van der Waals heterostructures tungsten disulfide/hexagonal boron nitride (vdWH WS2/h-BN). The h-BN and WS2 were modified with poly (diallyldimethylammonium chloride) (PDDA) and sodium dodecyl benzene sulfonate (SDBS) to obtain the positively charged PDDA@h-BN and the negatively charged SDBS@WS2, respectively. When the mass ratio of PDDA to h-BN and SDBS to WS2 were both 1:1 and the pH was 3, the zeta potential of PDDA@h-BN and SDBS@WS2 were 60.0 mV and −50.1 mV, respectively. Under the electrostatic interaction, the PDDA@h-BN and SDBS@WS2 attracted each other and stacked alternately along the (002) crystal plane forming the multi-layer (four-layer) vdWH WS2/h-BN. The addition of the multi-layer vdWH WS2/h-BN (1.0 wt%) to the base oil resulted in a significant reduction of 33.8% in the friction coefficient (0.104) and 16.8% in the wear rate (4.43 × 10−5 mm3/(N·m)). The excellent tribological property of the multi-layer vdWH WS2/h-BN arose from the lattice mismatch (26.0%), a 15-fold higher interlayer slip possibility, and the formation of transfer film at the contact interface. This study provided an easily accessible method for the multi-layer vdWH with excellent tribological properties.","PeriodicalId":502914,"journal":{"name":"Lubricants","volume":"29 16","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2024-05-07","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Preparation and Tribological Performance of Multi-Layer van der Waals Heterostructure WS2/h-BN\",\"authors\":\"Yunqi Fang, Yang Sun, Fengqin Shang, Jing Zhang, Jiayu Yao, Zihan Yan, Hangyan Shen\",\"doi\":\"10.3390/lubricants12050163\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Van der Waals heterostructures with incommensurate contact interfaces show excellent tribological performance, which provides solutions for the development of new solid lubricants. In this paper, a facile electrostatic layer-by-layer self-assembly (LBL) technique was proposed to prepare multi-layer van der Waals heterostructures tungsten disulfide/hexagonal boron nitride (vdWH WS2/h-BN). The h-BN and WS2 were modified with poly (diallyldimethylammonium chloride) (PDDA) and sodium dodecyl benzene sulfonate (SDBS) to obtain the positively charged PDDA@h-BN and the negatively charged SDBS@WS2, respectively. When the mass ratio of PDDA to h-BN and SDBS to WS2 were both 1:1 and the pH was 3, the zeta potential of PDDA@h-BN and SDBS@WS2 were 60.0 mV and −50.1 mV, respectively. Under the electrostatic interaction, the PDDA@h-BN and SDBS@WS2 attracted each other and stacked alternately along the (002) crystal plane forming the multi-layer (four-layer) vdWH WS2/h-BN. The addition of the multi-layer vdWH WS2/h-BN (1.0 wt%) to the base oil resulted in a significant reduction of 33.8% in the friction coefficient (0.104) and 16.8% in the wear rate (4.43 × 10−5 mm3/(N·m)). The excellent tribological property of the multi-layer vdWH WS2/h-BN arose from the lattice mismatch (26.0%), a 15-fold higher interlayer slip possibility, and the formation of transfer film at the contact interface. This study provided an easily accessible method for the multi-layer vdWH with excellent tribological properties.\",\"PeriodicalId\":502914,\"journal\":{\"name\":\"Lubricants\",\"volume\":\"29 16\",\"pages\":\"\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2024-05-07\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Lubricants\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.3390/lubricants12050163\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Lubricants","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.3390/lubricants12050163","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Preparation and Tribological Performance of Multi-Layer van der Waals Heterostructure WS2/h-BN
Van der Waals heterostructures with incommensurate contact interfaces show excellent tribological performance, which provides solutions for the development of new solid lubricants. In this paper, a facile electrostatic layer-by-layer self-assembly (LBL) technique was proposed to prepare multi-layer van der Waals heterostructures tungsten disulfide/hexagonal boron nitride (vdWH WS2/h-BN). The h-BN and WS2 were modified with poly (diallyldimethylammonium chloride) (PDDA) and sodium dodecyl benzene sulfonate (SDBS) to obtain the positively charged PDDA@h-BN and the negatively charged SDBS@WS2, respectively. When the mass ratio of PDDA to h-BN and SDBS to WS2 were both 1:1 and the pH was 3, the zeta potential of PDDA@h-BN and SDBS@WS2 were 60.0 mV and −50.1 mV, respectively. Under the electrostatic interaction, the PDDA@h-BN and SDBS@WS2 attracted each other and stacked alternately along the (002) crystal plane forming the multi-layer (four-layer) vdWH WS2/h-BN. The addition of the multi-layer vdWH WS2/h-BN (1.0 wt%) to the base oil resulted in a significant reduction of 33.8% in the friction coefficient (0.104) and 16.8% in the wear rate (4.43 × 10−5 mm3/(N·m)). The excellent tribological property of the multi-layer vdWH WS2/h-BN arose from the lattice mismatch (26.0%), a 15-fold higher interlayer slip possibility, and the formation of transfer film at the contact interface. This study provided an easily accessible method for the multi-layer vdWH with excellent tribological properties.